Microstructure and Residual Stresses in a Friction Stir Welded Butt Joint of as-cast ZK60 Alloy Containing Rare Earths

Texto completo
Autor(es):
Erenilton Pereira da Silva [1] ; Verona Biancardi Oliveira [2] ; Victor Ferrinho Pereira [3] ; Omar Maluf [4] ; Ricardo Henrique Buzolin [5] ; Haroldo Cavalcanti Pinto [6]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] University of São Paulo. Engineering School of São Carlos. Department of Materials Engineering - Brasil
[2] University of Rio de Janeiro State. Polytecnic Institute. Department of Materials - Brasil
[3] Brazilian Nanotechnology National Laboratory - Brasil
[4] Faculty of Technology of Sertãozinho - Brasil
[5] University of São Paulo. Engineering School of São Carlos. Department of Materials Engineering - Brasil
[6] University of São Paulo. Engineering School of São Carlos. Department of Materials Engineering - Brasil
Número total de Afiliações: 6
Tipo de documento: Artigo Científico
Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 20, n. 3, p. 775-779, 2017-04-27.
Resumo

The effect of a travel speed of 200 mm/min as well as a tool rotational speed of 1200 rpm on butt joint quality of friction stir welding (FSW) ZK60 magnesium casting alloy containing 1.5 wt.% rare earths (ZK60-1.5RE) was investigated to determine microstructure and residual stresses. FSW results in the generation of heterogeneous metallurgical structures consisting of the base material (BM), stirred zone (SZ) and thermo-mechanical affected zone (TMAZ). The stirring action also produced a non-uniform distribution and segregation of intermetalics. The transversal distribution of the longitudinal welding stresses exhibits a "M-like" shape with mostly tensile stresses under the shoulder region and only one compressive stress peak in the advancing side of the SZ and TMAZ. It could be demonstrated that FSW of ZK60-1.5RE alloy was successful in the welding conditions applied during the present work. (AU)

Processo FAPESP: 11/19218-0 - Fundição, tratamento térmico e caracterização de ligas de magnésio ZK60-RE para aplicações em estruturas aeronáuticas
Beneficiário:Ivan Feierabend
Modalidade de apoio: Bolsas no Brasil - Iniciação Científica
Processo FAPESP: 11/09324-8 - Junção por fricção e mistura mecânica em ligas tixofundidas de magnésio de alto desempenho
Beneficiário:Erenilton Pereira da Silva
Modalidade de apoio: Bolsas no Brasil - Doutorado Direto
Processo FAPESP: 10/11391-2 - Junção por fricção e mistura mecânica em ligas tixofundidas de magnésio de alto desempenho
Beneficiário:Haroldo Cavalcanti Pinto
Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores