Hydrogen storage properties of 2Mg-Fe mixtures processed by hot extrusion at different temperatures

Texto completo
Autor(es):
de Lima Andreani, G. F. ; Miglioli, M. M. ; Triques, M. R. M. ; Roche, V. ; Kiminami, C. S. ; Botta, W. J. ; Jorge, Jr., A. M.
Número total de Autores: 7
Tipo de documento: Artigo Científico
Fonte: INTERNATIONAL JOURNAL OF HYDROGEN ENERGY; v. 42, n. 16, p. 11493-11500, APR 20 2017.
Citações Web of Science: 4
Resumo

2Mg-Fe mixtures produced by high-energy ball milling were consolidated into bulk form by hot extrusion at different processing temperatures (573 K (300 degrees C), 623 K (350 degrees C) and 673 K (400 degrees C)), aiming to evaluate their influence on the structure and microstructure of bulk materials and their consequent influence on the hydrogen sorption properties. In spite being in the nanosize range, the highest the processing temperature, the larger the grain sizes. However, the nanometric grain size remained after any hot extrusion condition, as estimated by Rietveld refinement. The pinning effect of Fe on Mg grain boundaries explained this effect. In the first absorption (activation), powders showed a hydrogen storage capacity of similar to 4.53 wt%, while the extruded samples (bulk materials) reached almost the same capacity during the period of hydrogenation (similar to 94% of the maximum hydrogen storage capacity for Mg2FeH6 - 5.5 wt%). The smallest crystallite sizes and highest surface area for hydrogenation explain the good performance of powders. However, when comparing only extruded samples, it was observed that the highest capacity and the lowest incubation times were mainly related to grain sizes and to the favorable texture along (002) plane of alpha Mg. The desorption temperature of bulk materials was very similar to that of powders, which is good considering the lower surface area of bulk materials. (C) 2017 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved. (AU)

Processo FAPESP: 13/05987-8 - Processamento e caracterização de ligas metálicas amorfas, metaestáveis e nano-estruturadas
Beneficiário:Claudio Shyinti Kiminami
Linha de fomento: Auxílio à Pesquisa - Temático
Processo FAPESP: 14/21237-1 - Caracterização das propriedades de armazenamento de hidrogênio de nanocompósitos à base de Mg maciços produzidos por extrusão em canal angular
Beneficiário:Gisele Ferreira de Lima Andreani
Linha de fomento: Auxílio à Pesquisa - Regular