Anelastic and optical properties of Bi0.5Na0.5TiO3 and (Bi0.5Na0.5)(0.94)Ba0.06TiO3 lead-free ceramic systems doped with donor Sm3+

Autor(es)

Camilo Albornoz Diaz, Julio Cesar ^[1] ; Venet, Michel ^[1] ; Cordero, Francesco ^[2] ; da Silva, Jr., Paulo Sergio ^[1]

Afiliação do(s) autor(es)

^[1] Univ Fed Sao Carlos, Dept Phys, Sao Carlos, SP - Brazil

^[2] CNR, ISC, Area Ric Roma Tor Vergata, Rome - Italy

• Tipo de documento: Artigo Científico
• Fonte: Journal of Alloys and Compounds; v. 746, p. 648-652, MAY 25 2018.
• Citações Web of Science: 0

Resumo

The effect of Sm3+ substitution in (Bi0.5Na0.5)((1-x))SmxTiO3 (BNT-100xSm) and {[}(Bi0.5Na0.5)(0.94)Ba-0.06]((1-x))SmxTiO3 (BNT6-100xSm) has been studied by conventional X-ray diffraction (XRD), mechanical spectroscopy and photoluminescence (PL) measures. Ceramic samples of BNT-100xSm (x = 0 and 0.02) and BNT6-100xSm (x = 0, 0.01, 0.02 and 0.04) were prepared via the conventional mixed-oxide method. X-ray diffraction patterns obtained for all the sintered samples at room temperature (RT) confirm the formation of perovskite structure without spurious phases. The BNT-0Sm and BNT-2Sm compositions have the same rhombohedral (R3c) crystalline structure at RT. The BNT6-0Sm composition is confirmed to be at the morphotropic phase boundary of the BNT-BT system, and when samarium is added, a clear evolution towards the tetragonal phase was observed, with corresponding disappearance of the rhombohedral peaks in XRD patterns. The analysis of the anelastic spectra indicate higher compositional disorder, reduction of tendency of the octahedra to tilt (in agreement with the stabilization of the tetragonal phase) and preferential substitution of Sm3+ in the position of Bi3+. New anomalies (induced by addition of Sm3+) are observed on the anelastic spectra. From the PL results we can confirm the presence of emissions corresponding to Sm3+ with small contribution of Sm2+, evidencing the different mechanisms for the charge balance needed in the donor doping. (C) 2018 Elsevier B.V. All rights reserved. (AU)

• Processo FAPESP: 12/08457-7 - Estudo das transições de fases de cerâmicas piezoelétricas livres de chumbo por espectroscopia mecânica
• Beneficiário: Paulo Sergio da Silva Junior
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 14/07375-2 - EMU concedido no projeto 2013/18719-1: sistema de medidas resolvidas no tempo
• Beneficiário: Marcio Daldin Teodoro
• Modalidade de apoio: Auxílio à Pesquisa - Programa Equipamentos Multiusuários
• Processo FAPESP: 13/00134-7 - Obtenção e aprimoramento das propriedades de compósitos magnetoelétricos livres de chumbo
• Beneficiário: Michel Venet Zambrano
• Modalidade de apoio: Auxílio à Pesquisa - Regular