On the severe localized corrosion susceptibility of the AA2198-T851 alloy

Autor(es)

de Sousa Araujo, Joao Victor ^[1] ; Donatus, Uyime ^[1] ; Queiroz, Fernanda Martins ^[2] ; Terada, Maysa ^[3] ; Milagre, Mariana Xavier ^[1] ; de Alencar, Maicon Cavalieri ^[1] ; Costa, Isolda ^[1]

Afiliação do(s) autor(es)

^[1] IPEN CNEN, Av Prof Lineu Prestes 2242, Sao Paulo - Brazil

^[2] Univ Sao Paulo, EPUSP, Ecola Politecn, Av Prof Mello Moraes 2463, Sao Paulo - Brazil

^[3] LNNano CNPEN, Brazilian Nanotechnoll Natl Lab, Rua Giuseppe Maximo Scolfaro, Campinas, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: Corrosion Science; v. 133, p. 132-140, APR 1 2018.
• Citações Web of Science: 14

Resumo

The time dependent susceptibility of AA2198-T851 Al-Cu-Li alloy to severe localized corrosion in 0.01 mol L-1 NaCl solution has been investigated by immersion and SVET tests. The results reveal that the propagation of severe localized corrosion, in the alloy, is crystallographic and it is associated with the slip bands in the individual grains of the alloy. The slip bands caused uneven precipitation of the active T1 particles. Also, oscillations in SVET current density values associated with deposition and detachment of corrosion products were observed. Furthermore, the intensity of corrosion activities increased over time for open or partially covered pits. (AU)

• Processo FAPESP: 17/03095-3 - Investigação da suscetibilidade à corrosão de ligas Al-Cu-Li com solda por atrito (FSW) utilizando a técnica de varredura do eletrodo vibratório (SVET)
• Beneficiário: Uyime Donatus
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 13/13235-6 - Estudo da corrosão localizada e caracterização da resistência à corrosão associada à fadiga na região de solda em ligas de alumínio de elevada resistência soldadas por fricção (FSW)
• Beneficiário: Isolda Costa
• Modalidade de apoio: Auxílio à Pesquisa - Temático