On the AA2198-T851 alloy microstructure and its correlation with localized corrosion behaviour

Autor(es)

Donatus, Uyime ^[1] ; Terada, Maysa ^{[2, 3]} ; Ospina, Carlos Ramirez ^[2] ; Queiroz, Fernanda Martins ^[1] ; Santos Bugarin, Aline Fatima ^[1] ; Costa, Isolda ^[1]

Afiliação do(s) autor(es)

^[1] Inst Pesquisas Energet & Nucl, Av Prof Lineu Prestes 2242, Sao Paulo - Brazil

^[2] CNPEM, Lab Nacl Nanotecnol LNNano, Rua Giuseppe MaximoScolfaro 10-000, BR-13083100 Campinas, SP - Brazil

^[3] Univ Sao Paulo, Escola Politecn, Av Prof Mello Moraes 2463, Sao Paulo, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: Corrosion Science; v. 131, p. 300-309, FEB 2018.
• Citações Web of Science: 23

Resumo

The corrosion behaviour of AA2198-T851 alloy has been investigated using a combination of immersion tests and different microscopy techniques. Results showed that severe localized corrosion initiated within 1 h of corrosion immersion test in 0.01 mol L-1 NaCl solution. The corrosion mechanism in this alloy is intragranular and it propagates crystallographically. The propagation occurs through grain orientation dependent bands and it can be likened to the movement of dislocation through slip planes. Corrosion rings around stable pits result from pH variations. Secondary pits form around primary pits within corrosion rings and are preceded by hydrogen evolution. (AU)

• Processo FAPESP: 13/13235-6 - Estudo da corrosão localizada e caracterização da resistência à corrosão associada à fadiga na região de solda em ligas de alumínio de elevada resistência soldadas por fricção (FSW)
• Beneficiário: Isolda Costa
• Modalidade de apoio: Auxílio à Pesquisa - Temático
• Processo FAPESP: 17/03095-3 - Investigação da suscetibilidade à corrosão de ligas Al-Cu-Li com solda por atrito (FSW) utilizando a técnica de varredura do eletrodo vibratório (SVET)
• Beneficiário: Uyime Donatus
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado