Phosphate glasses via coacervation route containing CdFe2O4 nanoparticles: structural, optical and magnetic characterization

Texto completo
Autor(es):
Orives, Juliane R. [1] ; Viali, Wesley R. [1] ; Santagneli, Silvia H. [1] ; Afonso, Conrado R. M. [2] ; Carvalho, Maria H. [3] ; de Oliveira, Adilson J. A. [3] ; Nalin, Marcelo [1]
Número total de Autores: 7
Afiliação do(s) autor(es):
[1] Sao Paulo State Univ UNESP, Inst Chem, POB 355, BR-14800060 Araraquara, SP - Brazil
[2] Fed Univ Sao Carlos UFSCar, Dept Mat Engn DEMa, BR-13565905 Sao Carlos, SP - Brazil
[3] Fed Univ Sao Carlos UFSCar, Dept Phys, POB 676, BR-13565905 Sao Carlos, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: DALTON TRANSACTIONS; v. 47, n. 16, p. 5771-5779, APR 28 2018.
Citações Web of Science: 2
Resumo

CdFe2O4 nanoparticles of around 3.9 nm were synthesized using the coprecipitation method and protected by a silica layer. The nanoparticles were mixed with a coacervate and transformed into phosphate glasses with 1, 4 and 8% in mass of nanoparticles by the melt-quenching method. TEM images confirm that the nanoparticles were successfully incorporated into the matrix without inducing crystallization. P-31 NMR and Raman spectral analyses show that new P-O-Si bonds are formed in the glasses containing nanoparticles. The glass transition increases as a function of the nanoparticle content due to an increase in the connectivity of the phosphate glass chains. The UV-Vis spectra show bands at 415 and 520 nm assigned to Fe3+ ions and at 1025 nm, characteristic of Fe2+ ions, indicating that some of the nanoparticles dissolve during the melting process. The sample with 8% CdFe2O4 presents a paramagnetic behavior. The glasses obtained are transparent, non-hygroscopic and possess enormous thermal stability which is important for the production of optical devices. (AU)

Processo FAPESP: 09/54082-2 - EMU: projeto para aquisição de um magnetômetro de amostra vibrante que utiliza como sensor um dispositivo supercondutor de interferência quântica acoplado (Squid-VSM) com circuito fechado de criogenia
Beneficiário:Ernesto Chaves Pereira de Souza
Linha de fomento: Auxílio à Pesquisa - Programa Equipamentos Multiusuários
Processo FAPESP: 13/07793-6 - CEPIV - Centro de Ensino, Pesquisa e Inovação em Vidros
Beneficiário:Edgar Dutra Zanotto
Linha de fomento: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs