Can TiF4 varnish or TiF4/NaF solution stain eroded and sound enamel?

Texto completo
Autor(es):
Mosquim, Victor [1] ; Pereira Santi, Larissa Rodrigues [2] ; de Souza, Beatriz Martines [2] ; Magalhaes, Ana Carolina [2]
Número total de Autores: 4
Afiliação do(s) autor(es):
[1] Univ Sao Paulo, Bauru Sch Dent, Dept Operat Dent Endodont & Dent Mat, Bauru, SP - Brazil
[2] Univ Sao Paulo, Bauru Sch Dent, Dept Biol Sci, Al Octavio Pinheiro Brisolla 9-75, BR-17012901 Bauru, SP - Brazil
Número total de Afiliações: 2
Tipo de documento: Artigo Científico
Fonte: Journal of Dentistry; v. 85, p. 11-17, JUN 2019.
Citações Web of Science: 0
Resumo

Objectives: This study evaluated the staining potential of TiF4 varnish and TiF4/NaF solution on both sound and previously eroded enamel in vitro. Methods: One hundred and eighty bovine enamel samples were polished; half of them remained sound and the other half was eroded (4 x 90s each, using a 0.1% citric acid). Thereafter, the baseline color reading was performed (T-0). The samples were then subdivided into the following treatments: TiF4 varnish (24,500 ppm F, 1 x 6 h), NaF varnish (24,500 ppm F, 1 x 6 h), placebo varnish (1 x 6 h), TiF4 /NaF solution (500 ppm F, 6 x 1 min), Erosion Protection-Eimex (R) (500 ppm F, 6 x 1 min) and control (water, 6 x 1 min). Between the applications, the samples were exposed to artificial saliva for 30 min. The color changes were measured immediately after the applications (T-1 -T-6) and after the exposure to artificial saliva (S-1 -S-6) by using a spectrophotometer (Vita EasyShade (R)). The Delta E-00 , L{*}, a{*} and b{*} data were compared using 2-way ANOVA/Tukey (p < 0.05). Results: TiF4 varnish induced significantly higher color change (Delta E-00) compared to NaF and placebo varnishes on sound enamel immediately after application, but not after saliva exposure. TiF4/NaF solution induced lower Delta E-00 values compared to control on sound enamel; however, no differences were found between TiF4/NaF and Elmex (R) . For eroded, no differences were seen between the tested varnishes and solutions. Both types of fluoride solutions increased the yellow appearance of enamel, while the varnishes did not. Conclusions: The color changes induced by the experimental TiF4 products are similar to the commercial ones. Clinical significance: Both TiF4 varnish and TiF4/NaF solution have shown staining potential similar to commercially available varnish (NaF) and solution (Elmex (R)) on sound and eroded enamel. These findings support the conduction of clinical trials, which, in the future, may lead to the commercialization of these products. (AU)

Processo FAPESP: 06/02540-9 - Avaliação clínica da efetividade de diferentes técnicas de clareamento em dentes polpados
Beneficiário:Rafael Francisco Lia Mondelli
Modalidade de apoio: Auxílio à Pesquisa - Regular
Processo FAPESP: 16/24538-8 - Avaliação do efeito de soluções experimentais para bochecho compostas por NaF e TiF4 sobre a erosão e abrasão dentária in situ
Beneficiário:Larissa Rodrigues Pereira Santi
Modalidade de apoio: Bolsas no Brasil - Iniciação Científica