Microstructural refinement of 355 aluminium alloys by ultrasonic melt treatment (UST)

Autor(es)

de Paula, Leandro Cassio ^[1] ; Zoqui, Eugenio Jose ^[1]

Afiliação do(s) autor(es)

^[1] Univ Estadual Campinas, UNICAMP, Sch Mech Engn, Mat & Mfg Dept, BR-13083860 Campinas, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: SN APPLIED SCIENCES; v. 1, n. 5 MAY 2019.
• Citações Web of Science: 1

Resumo

Chemical grain refining of high-silicon-content aluminium alloys, such as 355 alloy, is impaired by the high silicon content. One solution is the use of ultrasonic melt treatment (UST). This study sought to determine the duration of UST and type of horn (steel or Ti) required to achieve optimal grain refining in these alloys. Samples produced by conventional casting underwent UST for different times with steel and Ti horns and were compared with as-cast samples. For all the conditions studied, analysis of the samples showed that UST is an effective grain refining technique and yields satisfactory values of average grain size and primary and secondary dendrite arm spacing (lambda(1), lambda(2)) as well as low porosity. The chemical composition of the samples was analysed by SEM-EDS mapping and point analysis to identify the intermetallic phases before and after UST. Best results were achieved after only 20 s of UST with a steel horn. UST for this length of time with a steel horn produced a homogeneous microstructure and possible homogeneous mechanical properties. Grain size was 160 mu m; primary dendrite arm spacing, or dendrite cell size, was 130 mu m; secondary arm spacing was approximately 18 mu m; and Vickers hardness was approximately 95 HV. (AU)

• Processo FAPESP: 15/22143-3 - Resistência à fadiga de ligas metálicas tixoconformadas
• Beneficiário: Eugênio José Zoqui