Improved densification and ionic conductivity in flash-sintered gamma-ray irradiated yttria-stabilized zirconia

Autor(es)

Muccillo, R. ^{[1, 2]} ; Muccillo, E. N. S. ^[2]

Afiliação do(s) autor(es)

^[1] Fed Univ ABC, BR-09210580 Santo Andre, SP - Brazil

^[2] Energy & Nucl Res Inst, Ctr Sci & Technol Mat, BR-05508170 Sao Paulo, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: SCRIPTA MATERIALIA; v. 170, p. 120-123, SEP 2019.
• Citações Web of Science: 0

Resumo

Experiments on electric field-assisted pressureless sintering were conducted, with a dilatometer connected to a power supply, in zirconia: 8 mol% yttria polycrystalline ceramics exposed to gamma radiation. During heating to 1000 degrees C, an electric field of 150 V cm(-1) was applied at room temperature up to a sharp thickness shrinkage occurred (flash sintering). It was found that the higher the imparted gamma radiation dose the higher the shrinkage. The shrinkage enhancement and the increase of the total ionic conductivity, when compared to non-irradiated sample, were probably due to the increase of oxygen vacancy concentration after exposure to gamma radiation. (C) 2019 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved. (AU)

• Processo FAPESP: 17/11937-4 - Rota sustentável para a conversão de metano com tecnologias eletroquímicas avançadas
• Beneficiário: Fabio Coral Fonseca
• Modalidade de apoio: Auxílio à Pesquisa - Programa Centros de Pesquisa em Engenharia
• Processo FAPESP: 13/07296-2 - CDMF - Centro de Desenvolvimento de Materiais Funcionais
• Beneficiário: Elson Longo da Silva
• Modalidade de apoio: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs