Evaluation of the Adhesion and Slurry Wear Erosion of Nb2O5 Coatings Applied by Flame Spray

Texto completo
Autor(es):
Xavier Belem, Maria Julia [1] ; Carvajal Fals, Hipolito [2] ; Sanchez Roca, Angel [2] ; Camello Lima, Carlos Roberto [1]
Número total de Autores: 4
Afiliação do(s) autor(es):
[1] Univ Metodista Piracicaba, Prod Engn Grad Program, BR-13451900 Piracicaba, SP - Brazil
[2] Oriente Univ, Coll Mech & Ind Engn, Santiago De Cuba 90900 - Cuba
Número total de Afiliações: 2
Tipo de documento: Artigo Científico
Fonte: METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE; v. 50, n. 12, p. 5877-5887, DEC 2019.
Citações Web of Science: 0
Resumo

Niobium pentoxide (Nb2O5) has excellent chemical and thermodynamic stabilities, characteristics that have accelerated the applications of this material in the form of coatings to protect against corrosive processes. However, few studies have evaluated its performance in wear protection applications. In this research, the slurry wear erosion resistance of Nb2O5 coatings deposited by flame spray was studied. The microstructural characterization of the coatings was performed by optical microscopy and scanning electron microscopy (SEM) assisted by chemical analysis by energy dispersive X-ray spectroscopy (EDS). Adhesion of the coatings was determined by the adhesion test (ASTM C633-13). Image analysis was used for the quantitative study of the adhesion tested areas and porosity of the coatings. Erosive wear resistance was determined using a container tribometer with erosive mixing at a particle velocity of 9.33 m/s and two particle incidence angles. The thinner coatings had fewer microstructural defects, such as pores and microcracks, and greater adhesive strength. The thicker coatings presented a cohesive failure mode. When the impact angle of the erodent particles was 90 deg, the thickness of the Nb2O5 coatings should not exceed 350 mu m. Nb2O5 coatings applied by flame spray showed good resistance to slurry wear erosion, besides inherent low cost and flexibility of the process. (AU)

Processo FAPESP: 17/25363-0 - Influência da adesão de revestimentos aplicados por distintos processos de aspersão térmica sobre suas propriedades de desgaste e corrosão
Beneficiário:Carlos Roberto Camello Lima
Linha de fomento: Auxílio à Pesquisa - Pesquisador Visitante - Internacional