Influence of Powder-to-Gel Ratio on Physicochemical Properties of a Calcium Silicate Sealer

Texto completo
Autor(es):
Torres, Fernanda F. E. [1] ; Perinoto, Patricia [1] ; Bosso-Martelo, Roberta [2] ; Chavez-Andrade, Gisselle M. [1] ; Guerreiro-Tanomaru, Juliane M. [1] ; Tanomaru-Filho, Mario [1]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Sao Paulo State Univ UNESP, Sch Dent, Dept Restorat Dent, Araraquara, SP - Brazil
[2] Fed Univ Bahia UFBA, Sch Dent, Integrated Clin Dept, Salvador, BA - Brazil
Número total de Afiliações: 2
Tipo de documento: Artigo Científico
Fonte: ODOVTOS INTERNATIONAL JOURNAL OF DENTAL SCIENCES; v. 22, n. 3, p. 154-162, SEP-DEC 2020.
Citações Web of Science: 0
Resumo

Differences in liquid-to-powder ratio can affect the properties of calcium silicate-based materials. This study assessed the influence of powder-to-gel ratio on physicochemical properties of NeoMTA Plus. Setting time (minutes), flow (mm and mm(2)), pH (at different periods), radiopacity (mm Al) and solubility (% mass loss) were evaluated using the consistencies for root repair material (NMTAP-RP; 3 scoops of powder to 2 drops of gel) and root canal sealer (NMTAP-SE; 3 scoops of powder to 3 drops of gel), in comparison to Biodentine cement (BIO) and TotalFill BC sealer (TFBC). Statistical analysis was performed using one-way ANOVA and Tukey tests (alpha=0.05). BIO had the shortest setting time, followed by NMTAP-RP and NMTAP-SE. TFBC showed the highest setting time and radiopacity. BIO, NMTAP-RP, and NMTAP-SE had similar radiopacity. All materials promoted an alkaline pH. NMTAP-RP/SE presented lower solubility than BIO and TFBC. Regarding the flow, TFBC had the highest values, followed by NMTAP-SE, and NMTAP-RP. BIO had the lowest flow. In conclusion, NMTAP in both powder-to-gel ratios showed high pH and low solubility. The increase in the powder ratio decreased the setting time and flow. These findings are important regarding the proper consistency and work time to clinical application. (AU)

Processo FAPESP: 15/03437-6 - Avaliação do preparo reciprocante, da obturação dos canais radiculares, e das propriedades físico-químicas e biológicas de materiais obturadores e reparadores
Beneficiário:Mario Tanomaru Filho
Linha de fomento: Auxílio à Pesquisa - Regular
Processo FAPESP: 17/19049-0 - Avaliação das etapas do tratamento de canais radiculares, e das propriedades físico-químicas e biológicas de materiais à base de silicato tricálcico
Beneficiário:Mario Tanomaru Filho
Linha de fomento: Auxílio à Pesquisa - Regular