The synergy effect of carbon/glass/epoxy hybrid laminate in Mode I delamination: A physical microfracture analysis

Autor(es)

Monticeli, Francisco Maciel ^[1] ; Shiino, Marcos Yutaka ^[2] ; Cornelis Voorwald, Herman Jacobus ^[1] ; Hilario Cioffi, Maria Odila ^[1]

Afiliação do(s) autor(es)

^[1] Sao Paulo State Univ Unesp, Sch Engn, Dept Mat & Technol, BR-12516410 Guaratingueta, SP - Brazil

^[2] Univ Estadual Paulista Unesp, Inst Ciencia & Tecnol, Dept Engn Ambiental, Sao Jose Dos Campos - Brazil

• Tipo de documento: Artigo Científico
• Fonte: ENGINEERING FRACTURE MECHANICS; v. 239, NOV 2020.
• Citações Web of Science: 0

Resumo

The adoption of carbon/glass fiber hybrid composites is an economical alternative to high-cost carbon/epoxy composites and helps to address environmental issues. However, the addition of another type of fiber modifies the mechanical behavior of the composite regarding interfacial interactions, consequently affecting other properties. Research related to three interfaces, with regard to hybrid composites, has not yet provided a good understanding of the physical interactions between components at a hybrid interface and how they affect the interfacial adhesion. In order to partially understand the interactions occurring in the proposed material, the fracture toughness in Mode I delamination was analyzed based on microstructural fracture mechanisms (FBZ) and energy balance principle models. The addition of flexible glass fiber in a stiffer carbon fiber lay-up enabled a considerable increase in the delamination strength. This property is also attributed to the organosilane adhesion promoter, a natural silane present in glass fiber. Additionally, the increased strain energy release is physically influenced by the rougher fracture surface and the hybrid fiber bridging failure mechanisms, inducing a more stable crack propagation and higher fracture toughness, compared to a carbon fiber composite. (AU)

• Processo FAPESP: 17/10606-4 - Fadiga em compósitos híbridos processados via RTM: influência da interface híbrida na delaminação nos modos I e II