Calcium Silicate-Based Experimental Sealers: Physicochemical Properties Evaluation

Autor(es)

Cristiane Lopes Zordan-Bronzel ^[1] ; Mario Tanomaru-Filho ^[2] ; Gisselle Moraima Chávez-Andrade ^[3] ; Fernanda Ferrari Esteves Torres ^[4] ; Giselle Priscilla Cruz Abi-Rached ^[5] ; Juliane Maria Guerreiro-Tanomaru ^[6]

Afiliação do(s) autor(es)

^[1] Universidade Estadual Paulista. Faculdade de Odontologia de Araraquara. Departamento de Odontologia Restauradora - Brasil

^[2] Universidade Estadual Paulista. Faculdade de Odontologia de Araraquara. Departamento de Odontologia Restauradora - Brasil

^[3] Universidade Estadual Paulista. Faculdade de Odontologia de Araraquara. Departamento de Odontologia Restauradora - Brasil

^[4] Universidade Estadual Paulista. Faculdade de Odontologia de Araraquara. Departamento de Odontologia Restauradora - Brasil

^[5] Universidade Estadual Paulista. Faculdade de Odontologia de Araraquara. Departamento de Odontologia Restauradora - Brasil

^[6] Universidade Estadual Paulista. Faculdade de Odontologia de Araraquara. Departamento de Odontologia Restauradora - Brasil

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 24, n. 1 2021-01-29.

Resumo

Abstract The aim of this study was to evaluate physicochemical properties of calcium silicate-based experimental (CS) endodontic sealers, developed using two different vehicles: polyethylene glycol (PG) (CS-PG) or polyethylene glycol associated to chitosan hydrogel (CS-PGCH). TotalFill BC Sealer (TF) and AH Plus (AHP) were evaluated for comparison. Setting time, flow, radiopacity, pH, solubility and volumetric change were analyzed. Data were submitted to ANOVA and Tukey tests with 5% significance level. The CS-PGCH had significantly greater setting time. CS-PG flow was similar to AHP. CS-PG had higher radiopacity than CS-PGCH. Calcium silicate-based sealers presented alkaline pH in all periods. CS-PGCH presented higher solubility in comparison with CS-PG. The volumetric change of CS-PG was similar to TF after 7 days, and to AHP after 30 days. CS-PG presented proper setting time, radiopacity, flow and pH, besides low volumetric change, showing better results than CS-PGCH, and potential for clinical application. (AU)

• Processo FAPESP: 17/19049-0 - Avaliação das etapas do tratamento de canais radiculares, e das propriedades físico-químicas e biológicas de materiais à base de silicato tricálcico
• Beneficiário: Mario Tanomaru Filho
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 17/14305-9 - Avaliação de novas substâncias para irrigação de canais radiculares e de cimentos endodônticos à base de silicato de cálcio
• Beneficiário: Juliane Maria Guerreiro Tanomaru
• Modalidade de apoio: Auxílio à Pesquisa - Regular