Magneto-optical borogermanate glasses and fibers containing Tb3+

Texto completo
Autor(es):
Franco, Douglas F. [1] ; Ledemi, Yannick [2] ; Correr, Wagner [2] ; Morency, Steeve [2] ; Afonso, Conrado R. M. [3] ; Messaddeq, Sandra H. [2] ; Messaddeq, Younes [1, 2] ; Nalin, Marcelo [1]
Número total de Autores: 8
Afiliação do(s) autor(es):
[1] Sao Paulo State Univ UNESP, Inst Chem, BR-14800060 Araraquara, SP - Brazil
[2] Univ Laval, Ctr Opt Photon & Laser, 2375 Rue Terrasse, Local 2131, Quebec City, PQ G1V 0A6 - Canada
[3] Fed Univ Sao Carlos UFSCar, Dept Mat Engn DEMa, Sao Carlos, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: SCIENTIFIC REPORTS; v. 11, n. 1 MAY 10 2021.
Citações Web of Science: 0
Resumo

New glass compositions containing high concentrations of Tb3+ ions were developed aiming at the production of magneto-optical (MO) fibers. This work reports on the structural and MO properties of a new glass composition based on (100 - x)(41GeO(2)-25B(2)O(3)-4Al(2)O(3)-10Na(2)O-20BaO) - xTb(4)O(7). Morphological analysis (HR-TEM) of the sample with the highest concentration of Tb3+ ions confirmed the homogeneous distribution of Tb3+ ions and the absence of nanoclusters. All the samples presented excellent thermal stability against crystallization (Delta T>100 degrees C). An optical fiber was manufactured by a fiber drawing process. The UV-Vis spectra of the glasses showed Tb3+ electronic transitions and optical windows varying from 0.4 to 1.6 mu m. The magneto-optical properties and the paramagnetic behaviors of the glasses were investigated using Faraday rotation experiments. The Verdet constant (V-B) values were calculated at 500, 650, 880, 1050, 1330, and 1550 nm. The maximum V-B values obtained at 650 and 1550 nm for the glass with x=18 mol% were -128 and - 17.6 rad T-1 m(-1), respectively. The V-B values at 500 and 1550 nm for the optical fiber containing 8 mol% of Tb4O7 were - 110.2 and - 9.5 rad T-1 m(-1), respectively, while the optical loss at around 880 nm was 6.4 dB m(-1). (AU)

Processo FAPESP: 16/16900-9 - Preparação de fibras de vidros óxidos de metal pesado com propriedades ópticas e magneto-ópticas
Beneficiário:Douglas Faza Franco
Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
Processo FAPESP: 13/07793-6 - CEPIV - Centro de Ensino, Pesquisa e Inovação em Vidros
Beneficiário:Edgar Dutra Zanotto
Modalidade de apoio: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs
Processo FAPESP: 18/19272-4 - Produção de fibras ópticas de metais pesados para uso em rotadores de Faraday
Beneficiário:Douglas Faza Franco
Modalidade de apoio: Bolsas no Exterior - Estágio de Pesquisa - Pós-Doutorado