Aerosol filtration performance of electrospun membranes comprising polyacrylonitrile and cellulose nanocrystals

Autor(es)

Santos, Rachel Passos de Oliveira ; Hao, Junli ; Frollini, Elisabete ; Savastano Junior, Holmer ; Rutledge, Gregory C.

• Tipo de documento: Artigo Científico
• Fonte: JOURNAL OF MEMBRANE SCIENCE; v. 650, p. 10-pg., 2022-05-15.

Resumo

Composite electrospun membranes of polyacrylonitrile (PAN) with contents of cellulose nanocrystals (CNCs) of 5-20 wt% were prepared. The increase in cellulose content improved the mechanical properties of the materials up to approximately 2-fold in the tensile strength and 6-fold in elastic modulus compared to the PAN membrane. Filtration performance of the composite membranes against aerosolized salt nanoparticles was evaluated under conditions relevant to their use as active layers in Filtering Facepiece Respirators (FFR), such as N95s. In general, all composite membranes presented values of filtration efficiency (FE) superior to 90%. Pressure drop (Delta p) values of the materials, in general, decreased with increasing content of CNCs. In general, an increase of the quality factor (QF) was observed with increasing content of CNCs in the membrane compositions, possibly due to a trend for the porosity of the composite materials to increase. The membrane containing 20 wt% of CNCs presented the highest QF (0.034 +/- 0.002 Pa-1), one of the highest FE of 95.97 +/- 0.62%, particle penetration (P) of 4.03 +/- 0.62%, and the lowest Delta p of 9.60 +/- 1.04 mmH2O. Thus, it is possible to prepare composite membranes of PAN reinforced with high content of natural, biodegradable, and abundant CNCs, and to evaluate comprehensively their potential to be used in air filtration applications such as respirators and cleanroom filters. (AU)

• Processo FAPESP: 17/19549-3 - Preparação de novos materiais para aplicação como sistemas de filtração e avaliação da sua eficiência em dispositivos de condicionamento de ar para edificações: Mats de nanofibras/fibras ultrafinas, sheets porosos e materiais multi-estruturados polimérico
• Beneficiário: Rachel Passos de Oliveira Santos
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 19/20626-8 - Membranas poliméricas reforçadas com celulose nanofibrilada e nanocristais de celulose: caracterização das propriedades micromecânicas e compressivas e avaliação da sua influência na filtração de aerossóis
• Beneficiário: Rachel Passos de Oliveira Santos
• Modalidade de apoio: Bolsas no Exterior - Estágio de Pesquisa - Pós-Doutorado