Bentonite functionalized with amine groups by the sol-gel route as efficient adsorbent of rhodamine-B and nickel (II)

Autor(es)

Pinos, Jessica Yasmin de Morais ; de Melo, Leticia Barbosa ; de Souza, Suelen Delfino ; Marcal, Liziane ; de Faria, Emerson Henrique

• Tipo de documento: Artigo Científico
• Fonte: APPLIED CLAY SCIENCE; v. 223, p. 12-pg., 2022-06-15.

Resumo

Environmental issues caused by population growth and increased industrial activity have become the object of criticism and discussion. This study evaluates how efficiently surfactant-modified bentonite bearing amine groups removes the metal nickel(II) and the dye rhodamine-B (RB) from wastewaters. First, hybrid inorganic organic materials were obtained by intercalation of a bentonite (Bent) with the surfactant cetyltrimethylammonium bromide (CTA), followed by functionalization with [N-3 (trimethoxysilyl)propyl] ethylenediamine (DAPTMS) by the sol-gel process. Then, the resulting materials were characterized by X-ray diffraction, infrared absorption spectroscopy, thermal analysis, specific surface area analysis, Small-Angle X-ray Scattering, and pHPZC and tested as adsorbents of Ni(II) or RB by the batch method. X-ray diffraction confirmed that the Bent interlayer space expanded after intercalation with CTA -the basal space varied from 1.3 nm in Bent to 1.8 nm in Bent-CTA and to 1.6 nm in Bent-CTA-DAPTMS. Infrared absorption spectroscopy attested that Bent-CTA-DAPTMS contained organosilane and surfactant: the spectra displayed bands at 2925, 2853, 1470 cm(-1), assigned to the CH2, CH3, and NH2 groups, respectively. The batch adsorption equilibrium experiments revealed that Bent and Bent-CTA-DAPTMS had higher adsorptive capacity for Ni(II) (q(t) = 65.77 mg g(-1)) and RB (qt = 0.98 mg g(-1)), respectively. The use of nonlinear equation models revealed that Ni(II) or RB adsorption onto the investigated materials followed pseudo-second-order kinetics, thereby confirming the high affinity between adsorbent and contaminants. (AU)

• Processo FAPESP: 17/15482-1 - Novas estratégias para o reaproveitamento de subprodutos de curtumes para a obtenção de materiais porosos funcionais de alto valor agregado
• Beneficiário: Emerson Henrique de Faria
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 12/11673-3 - Obtenção de filmes finos por spin e dip-coating usando a metodologia sol-gel
• Beneficiário: Eduardo José Nassar
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 16/01501-1 - Catalisadores multifuncionais para processos oxidativos avançados empregando matrizes biogênicas ou argilas
• Beneficiário: Katia Jorge Ciuffi Pires
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 11/03335-8 - Ferroporfirinas como catalisadores em reações de oxidação do ciclohexano e reação de "Bayer-Villiger: sistemas heterogêneos
• Beneficiário: Katia Jorge Ciuffi Pires
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 98/11022-3 - Oxidacao catalitica biomimetica.
• Beneficiário: Katia Jorge Ciuffi Pires
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 13/19523-3 - Materiais biohíbridos funcionais baseados em argilas lamelares e/ou fibrosas com aplicações multifacetadas
• Beneficiário: Emerson Henrique de Faria
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 05/00720-7 - Síntese, caracterização e atividade catalítica de sistemas biomiméticos e não-biomiméticos em reações de oxidação de hidrocarbonetos, utilizando o peróxido de hidrogênio como oxidante
• Beneficiário: Katia Jorge Ciuffi Pires
• Modalidade de apoio: Auxílio à Pesquisa - Regular