Autor(es)

Spitznagel, Frank A. ; Bonfante, Estevam A. ; Campos, Tiago M. B. ; Vollmer, Maximilian A. ; Boldt, Johannes ; Doerken, Sam ; Gierthmuehlen, Petra C.

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS; v. 14, n. 24, p. 13-pg., 2021-12-01.

Resumo

To evaluate the failure-load and survival-rate of screw-retained monolithic and bi-layered crowns bonded to titanium-bases before and after mouth-motion fatigue, 72 titanium-implants (SlCvantage-max, SIC-invent-AG) were restored with three groups (n = 24) of screw-retained CAD/CAM implant-supported-single-crowns (ISSC) bonded to titanium-bases: porcelain-fused-to-metal (PFM-control), porcelain-fused-to-zirconia (PFZ-test) and monolithic LDS (LDS-test). Half of the specimens (n = 12/group) were subjected to fatigue in a chewing-simulator (1.2 million cycles, 198 N, 1.67 Hz, thermocycling 5-55 degrees C). All samples were exposed to single-load-to-failure without (PFM0, PFZ0, LDS0) or with fatigue (PFM1, PFZ1, LDS1). Comparisons were statistically analyzed with t-tests and regression-models and corrected for multiple-testing using the Student-Neuman- Keuls method. All PFM and LDS crowns survived fatigue exposure, whereas 16.7% of PFZ showed chipping failures. The mean failure-loads (+/- SD) were: PFM0: 2633 +/- 389 N, PFM1: 2349 +/- 578 N, PFZ0: 2152 +/- 572 N, PFZ1: 1686 +/- 691 N, LDS0: 2981 +/- 798 N, LDS1: 2722 +/- 497 N. Fatigue did not influence load to failure of any group. PFZ ISSC showed significantly lower failure-loads than monolithic-LDS regardless of artificial aging (p < 0.05). PFM ISSC showed significantly higher failure loads after fatigue than PFZ (p = 0.032). All ISSC failed in a range above physiological chewing forces. Premature chipping fractures might occur in PFZ ISSC. Monolithic-LDS ISSC showed high reliability as an all-ceramic material for screw-retained posterior hybrid-abutment-crowns. (AU)

• Processo FAPESP: 12/19078-7 - Desenvolvimento e processamento de compósito de Al2O3-ZrO2 para próteses monolíticas CAD/CAM: efeito do envelhecimento na resistência à flexão biaxial
• Beneficiário: Estevam Augusto Bonfante
• Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores
• Processo FAPESP: 16/18818-8 - EMU concedido no processo 2012/19078-7: ElectroPuls E3000 Linear-Torsion All-Electric dynamic test instrument package
• Beneficiário: Estevam Augusto Bonfante
• Modalidade de apoio: Auxílio à Pesquisa - Programa Equipamentos Multiusuários