Microstructural Characterization of Maraging 300 Steel Fabricated by Select Laser Melting

Texto completo
Autor(es):
Rodriguez, J. ; Hoyos, E. ; Conde, F. ; Jardini, A. L. ; Oliveira, J. P. ; Avila, J. ; Minerals, Met & Mat Soc
Número total de Autores: 7
Tipo de documento: Artigo Científico
Fonte: TMS 2021 150TH ANNUAL MEETING & EXHIBITION SUPPLEMENTAL PROCEEDINGS; v. N/A, p. 8-pg., 2021-01-01.
Resumo

printing of components using a layer-based deposition of materials is referred to as additive manufacturing (AM). The ability to build complex geometry components, reduce waste and avoid assembly are the main advantages of this process. AM has been used in different industries like aerospace, medical, goods and automotive. In the aerospace, materials with high performance are needed to fulfill the requirements of the industry. Maraging steels are among the materials widely used for several applications in the aerospace industry due to its high strength and toughness. These steels are hardened by the precipitation of intermetallics in a martensitic matrix. In this work, a maraging 300 steel powder was used to produce components by selective laser melting (SLM). Two heat treatments were applied to study the martensite-to-austenite reversion, HT1: 480 degrees C/3 h and HT2: 980 degrees C/1 h + 2 x 690 degrees C/5 min + 480 degrees C/6 h. The microstructural characterization was assessed by optical microscopy (OM), scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD). As-built condition revealed a cellular and dendritic morphology with segregation of Ti, Ni and Mo to the grain boundaries. Direct aging treatment does not erase the typical AM morphology, but a solubilization at 980 degrees C/1 h was capable of fully recrystallize the microstructure. The EBSD analysis showed the increase of reverted austenite for the HT2 and this was attributed to the cycling reversion. (AU)

Processo FAPESP: 08/57860-3 - BIOFABRIS - Instituto de Biofabricação
Beneficiário:Rubens Maciel Filho
Modalidade de apoio: Auxílio à Pesquisa - Temático
Processo FAPESP: 17/17697-5 - Avaliação mecânica e microestrutural de peças fabricadas por manufatura aditiva no aço 18%Ni Maraging 300 com aplicação aeronáutica.
Beneficiário:Julian Arnaldo Avila Diaz
Modalidade de apoio: Auxílio à Pesquisa - Regular