Effect of Xylitol Varnishes on the Inhibition of Demineralization in Vitro

Autor(es)

Naves, Paula Andery ; de Moura, Alexandre Lima ; Rodrigues, Marcela Charantola ; Diniz, Michele Baffi ; Arana-Chavez, Victor Ellias ; Jordao, Maisa Camillo ; Cardoso, Cristiane de Almeida Baldini

• Tipo de documento: Artigo Científico
• Fonte: PESQUISA BRASILEIRA EM ODONTOPEDIATRIA E CLINICA INTEGRADA; v. 22, p. 9-pg., 2022-01-01.

Resumo

Objective: To evaluate the efficacy of xylitol varnishes in the inhibition of enamel demineralization in vitro. Material and Methods: Bovine enamel blocks (n=120) were randomly allocated to four groups (n = 30), and the surface hardness (SH) was measured at baseline. The blocks were treated with the following varnishes: 20% xylitol, 20% xylitol plus F (5% NaF), DuraphatTM (5% NaF, positive control), and placebo (no-F/xylitol, negative control). The varnishes were applied and removed after 6 h of immersion in artificial saliva. The blocks were subjected to pH cycles (demineralization and remineralization for 2 and 22h/day, respectively, for 8 days). Surface and cross-sectional hardnesses were measured to calculate the percentage of SH loss (%SHL) and the integrated loss of the subsurface hardness (Delta KHN). Data were statistically analyzed using Kruskal-Wallis and Tukey's tests (p<0.05). Results: %SHL was significantly decreased by 20% xylitol plus F, DuraphatTM, and 20% xylitol varnishes compared to placebo. The use of 20% xylitol plus F varnish led to a significantly lower percentage of SH loss compared to the use of 20% xylitol varnish without F. However, the experimental and commercial varnishes led to significantly lower subsurface demineralization compared to placebo and did not differ from each other. Conclusion: Xylitol varnishes, especially when combined with F, effectively prevent enamel demineralization. (AU)

• Processo FAPESP: 13/09533-1 - Vernizes contendo xilitol e/ou fluoreto para controle da cárie dentária: estudos in vitro, in situ e clínico randomizado.
• Beneficiário: Cristiane de Almeida Baldini Cardoso
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado