The Influence of Implant Design Features on the Bone Healing Pathway: An Experimental Study in Sheep

Texto completo
Autor(es):
Bergamo, Edmara T. P. ; de Oliveira, Paula G. F. P. ; Jimbo, Ryo ; Neiva, Rodrigo ; Gil, Luiz F. ; Tovar, Nick ; Wtek, Lukasz ; Bonfante, Estevam A. ; Coelho, Paulo G.
Número total de Autores: 9
Tipo de documento: Artigo Científico
Fonte: INTERNATIONAL JOURNAL OF PERIODONTICS & RESTORATIVE DENTISTRY; v. 43, n. 3, p. 8-pg., 2023-05-01.
Resumo

This study evaluated how implant design features influence osseointegration. Two implant macrogeometries and surface treatments were evaluated: (1) progressive buttress threads with an SLActive surface (SLActive/BL), and (2) inner and outer trapezoidal threads with a nanohydroxyapatite coating over a dual acid-etched surface (Nano/U). Implants were placed in the right ilium of 12 sheep, and histologic and-metric analyses were conducted after 12 weeks. Percentages of bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO) within the threads were quantified. Histologically, the SLActive/BL group showed greater and more intimate BIC than the Nano/U group. In contrast, Nano/U group depicted woven bone formation within the healing chambers, between the osteotomy wall and implant threads, and bone remodeling was evident at the outer thread tip. Significantly higher BAFO was seen in the Nano/U group than the SLActive/BL group at 12 weeks (P < .042). Different implant design features influenced the osseointegration pathway, supporting further investigations to describe the differences and clinical performance. Int J Periodontics Restorative Dent 2023;43:337-343. doi: 10.11607/prd.5438 (AU)

Processo FAPESP: 12/19078-7 - Desenvolvimento e processamento de compósito de Al2O3-ZrO2 para próteses monolíticas CAD/CAM: efeito do envelhecimento na resistência à flexão biaxial
Beneficiário:Estevam Augusto Bonfante
Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores
Processo FAPESP: 21/06730-7 - Rumo à zircônia sustentável reciclada a partir do descarte de usinagem e melhorada por infiltração graduada e ao desenvolvimento de blocos de zircônia multicamada resistentes, graduados, e não suscetíveis ao envelhecimento
Beneficiário:Estevam Augusto Bonfante
Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores - Fase 2
Processo FAPESP: 19/08693-1 - Compósitos experimentais à base de alumina e zircônia infiltrados por vidro: caracterização microestrutural e das propriedades ópticas e mecânicas.
Beneficiário:Edmara Tatiely Pedroso Bergamo
Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado