Dentin Microhardness and Subsurface Morphology After Er:YAG Laser Cavity Preparation Using Different Parameters

Autor(es)

Souza-Gabriel, Aline Evangelista ; Chinelatti, Michelle Alexandra ; Pecora, Jesus Djalma ; Palma-Dibb, Regina Guenka ; Milori Corona, Silmara Aparecida

• Tipo de documento: Artigo Científico
• Fonte: JOURNAL OF DENTISTRY FOR CHILDREN; v. 76, n. 1, p. 9-pg., 2009-01-01.

Resumo

Purpose: The purpose of this study was to evaluate the influence of the Er:YAG laser, using different parameters, on dentin microhardness and subsurface morphology. Methods: One hundred thirty dentin fragments were randomly assigned to 13 groups: 12 received laser irradiation with different energies (200, 250, 300, or 350 mJ) and pulse repetition rates (2, 3, or 4 Hz); and 1 (control) was prepared using a carbide bur. Specimens were bisected. One hemisection was fixed with the subsurface face up and polished. The other one was prepared for scanning electron microscopy. The microhardness test was performed at 5 depths (30, 60, 90, 120, and 150 mu m) and 7 points (6 in the cavity edges and 1 in a nonirradiated area). Data were tested by analysis of variance and Tukey test. Results: The highest microhardness values were recorded for lased-irradiated groups with 250 mJ/4 Hz and 350 mJ/4 Hz, only in the deep region of the cavity and until 60 mu m. The parameters 300 mJ/3 Hz, 350 mJ/3 Hz, and 200 mJ/4 Hz changed the morphology until 10 mu m; and 250 mJ/4 Hz, 300 mJ/4 Hz, and 350 mJ/4 Hz until 30 mu m (P=0.0328). The bur-prepared group displayed the lowest microhardness values, being statistically similar to 200 mJ/2 Hz (P=0.1824), and the subsurface did not exhibit morphological alterations. Conclusions: The Er:YAG laser with 250 mJ/4 Hz and 350 mJ/4 Hz increased dentin microhardness in the deepest area of the cavity until 60 mu m. Use of the lower parameters (200 mJ/2 Hz, 250 mJ/2 Hz, or 300 mJ/2 Hz) to prepare dentin with the Er: YAG laser produced results similar to those for bur-prepared cavities. (AU)

• Processo FAPESP: 03/03780-5 - Estudo in vitro da influência da energia e frequência do laser Er:YAG na microdureza das paredes cavitárias de esmalte e dentina após o preparo
• Beneficiário: Aline Evangelista de Souza Gabriel
• Modalidade de apoio: Bolsas no Brasil - Mestrado