| Resumo | |
ZrB2 is a nonsuperconducting Pauli paramagnetic crystallizing in the AlB2 structure. V substitution for Zr in Zr1-xVxB2 (0.01 <= x <= 0.1) at the few percentage level induces superconductivity with critical temperature reaching a maximum of 8.7 K for Zr0.96V0.04B2 near the solid solubility limit. Specific-heat and lower critical field temperature dependence results suggest the possibility of unconventional superconductivity possibly arising from multiband effects. (AU) | |
| Processo FAPESP: | 09/54001-2 - EMU: aquisição de equipamento cryo-free para caracterização de propriedades magnéticas por magnetometria de amostra vibrante (VSM) |
| Beneficiário: | Carlos Alberto Moreira dos Santos |
| Modalidade de apoio: | Auxílio à Pesquisa - Programa Equipamentos Multiusuários |
| Processo FAPESP: | 10/11770-3 - Estudo da estrutura de defeitos em diboretos de metais de transição (MeB2) e sua relação com o comportamento supercondutor. |
| Beneficiário: | Antonio Jefferson da Silva Machado |
| Modalidade de apoio: | Auxílio à Pesquisa - Regular |
| Processo FAPESP: | 11/05961-3 - Estudo da supercondutividade em diboretos e dicalcogenios de metais de transição (MeB2 e MeX2), com protótipo AlB2 e suas variações |
| Beneficiário: | Sérgio Tuan Renosto |
| Modalidade de apoio: | Bolsas no Brasil - Doutorado |