| Fonte: | Integrated Ferroelectrics; v. 174, n. 1, p. 11-pg., 2016-01-01. |
| Resumo | |
The influence of ferromagnetic phase properties on the magnetoelectric response of hot pressed particulate composites formed by 80mol% of 0.675[Pb(Mg1/3Nb2/3)O-3]-0.325[PbTiO3] as piezoelectric matrix and 20mol% of NiFe2O4, CoFe2O4 or BaFe12O19 phases was analyzed. The hot pressing sintering method was suitable for obtaining composites with apparent density higher than 94% and electric resistivity close to 10(9) .m, independently of the ferromagnetic phases used. The magnitude of the magnetoelectric coupling seems to be governed by the piezoelectric properties of ferroelectric PMN-PT matrix, and the zero bias magnetoelectric coefficient values are determined by the ferromagnetic hardness of the magnetic phase. (AU) | |
| Processo FAPESP: | 08/04025-0 - Materiais multifuncionais multiferróicos nanoestruturados: síntese, propriedades, fenomenologia e aplicações |
| Beneficiário: | José Antonio Eiras |
| Modalidade de apoio: | Auxílio à Pesquisa - Temático |
| Processo FAPESP: | 10/07518-7 - Efeito de tamanho no acoplamento magnetoelétrico em materiais multiferróicos compósitos nanoestruturados |
| Beneficiário: | Fabio Luis Zabotto |
| Modalidade de apoio: | Bolsas no Brasil - Pós-Doutorado |