Influence of Surface Crystalline Structures on DSC Analysis of PTFE

Autor(es)

Sciuti, Vinicius Fiocco ; Melo, Caiua Caldeira ; Canto, Leonardo Bresciani ; Canto, Rodrigo Bresciani

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 20, n. 5, p. 10-pg., 2017-09-01.

Resumo

The physical and mechanical properties of polytetrafluorethylene (PTFE) are greatly dependent on the degree of crystallinity and this is extremely important for the modeling of PTFE processing which is complex and costly. Differential scanning calorimetry (DSC) is one of the most important techniques for the determination of the degree of crystallinity and powder granules of the sample are generally used in the analysis. This procedure provides samples with a high surface-to-volume ratio, resulting in the formation of a considerable number of surface crystalline structures, called warts, along with the bulk crystallization, as shown by scanning electron microscopy. The presence of warts has a significant effect on the PTFE melting enthalpy and thus hinders the correct estimation of the degree of crystallinity of industrial PTFE parts, in which bulk crystallization prevails. In this study, we propose a procedure which does not lead to the formation of warts in the DSC sample and thus allows a more accurate determination of the melting enthalpy (or the degree of crystallinity) of industrial PTFE parts. We demonstrate that samples must be extracted from the core of dense (well-pressed) parts previously sintered in an oven, and the use of powder granules and/or sintering in DSC is not recommended. (AU)

• Processo FAPESP: 13/00256-5 - Aperfeiçoamento e validação de modelos numéricos para a simulação da prensagem a frio do politetrafluoretileno (PTFE)
• Beneficiário: Caiuã Caldeira de Melo
• Modalidade de apoio: Bolsas no Exterior - Estágio de Pesquisa - Iniciação Científica
• Processo FAPESP: 12/10319-1 - Comportamento mecânico do politetrafluoretileno (PTFE) sob diferentes taxas de deformação em tração e compressão simples
• Beneficiário: Vinicius Fiocco Sciuti
• Modalidade de apoio: Bolsas no Brasil - Iniciação Científica
• Processo FAPESP: 12/25374-8 - Identificação e validação de um modelo de comportamento mecânico para o PTFE
• Beneficiário: Vinicius Fiocco Sciuti
• Modalidade de apoio: Bolsas no Exterior - Estágio de Pesquisa - Iniciação Científica
• Processo FAPESP: 10/20925-0 - Desenvolvimento de um sistema experimental para validação de modelos numéricos de compactação do politetrafluoretileno (PTFE)
• Beneficiário: Caiuã Caldeira de Melo
• Modalidade de apoio: Bolsas no Brasil - Iniciação Científica