Microstructural Stability of a Niobium Single Crystal Deformed by Equal Channel Angular Pressing

Autor(es)

Bernardi, Heide Heloise ; Zschommler Sandim, Hugo Ricardo ; Zilnyk, Kahl Dick ; Verlinden, Bert ; Raabe, Dierk

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 20, n. 5, p. 10-pg., 2017-09-01.

Resumo

A [211]-oriented niobium single crystal was deformed by equal channel angular pressing (ECAP) at room temperature using the route B-c to a total strain of 9.2. A sharp cube texture develops after ECAP processing. The deformed samples were annealed in vacuum from 400 degrees C (673 K) to 900 degrees C (1173 K) for 1 h to evaluate their microstructural stability. Scanning electron microscopy (SEM) was used to image the microstructures of as-deformed and annealed specimens. Electron backscatter diffraction (EBSD) was employed to determine the respective microtextures before and after annealing. Coarsening of the microstructure occurs at a maximum rate at 550 degrees C (823 K) due to discontinuous recrystallization. Normal grain growth replaces discontinuous recrystallization as the main coarsening mechanism above 700 degrees C (973 K). (AU)

• Processo FAPESP: 04/14875-0 - Processamento e caracterização microestrutural de nióbio deformado plasticamente por extrusão em canal angular
• Beneficiário: Heide Heloise Bernardi
• Modalidade de apoio: Bolsas no Brasil - Doutorado Direto