Nanostructured bulk HPT β Ti-42Nb alloy as biomaterial for implants obtained directly from micrometric powders

Autor(es)

Kuroda, Pedro A. B. ; Carvalho, Amanda P. ; Caram, Rubens ; Figueiredo, Roberto B. ; Afonso, Conrado R. M.

• Tipo de documento: Artigo Científico
• Fonte: Materials Letters; v. 378, p. 4-pg., 2024-10-25.

Resumo

The effect of high-pressure torsion (HPT) processing on mechanical properties in a (3 Ti-42Nb alloy micrometric powder consolidated in a nanostructured bulk disc through severe plastic deformation for biomedical applications is investigated. XRD, SEM and TEM/ASTAR characterization are used to characterize microstructure of the original micrometric powder and the consolidated disc of (3 Ti-42Nb alloy after HPT. The results show that severe plastic deformation processing improves Vickers hardness of (3 Ti-42Nb alloy, and leads to a low modulus bulk material with E = 63 GPa after HPT, comparable with that of as-cast alloy. The obtaining of nanostructured grain size around 55 nm bulk (3 Ti-42Nb alloy consolidated through HPT from micrometric atomized powder opens perspectives of applications as biomedical implants. (AU)

• Processo FAPESP: 18/18293-8 - Ligas de titânio: transformações de fases e manufatura aditiva aplicadas na obtenção de materiais com gradientes funcionais
• Beneficiário: Rubens Caram Junior
• Modalidade de apoio: Auxílio à Pesquisa - Temático
• Processo FAPESP: 19/26517-6 - Influência da microestrutura e fases formadas na funcionalização da superfície de ligas beta Ti-25Ta-xZr
• Beneficiário: Pedro Akira Bazaglia Kuroda
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 21/03756-5 - Ligas avançadas de magnésio para aplicações de suporte de carga em Medicina
• Beneficiário: Andrea Madeira Kliauga
• Modalidade de apoio: Auxílio à Pesquisa - Regular