Ethanol Electrooxidation using Ti/(RuO2)((x)) Pt(1-x) Electrodes Prepared by the Polymeric Precursor Method

Autor(es)

Freitas, R. G. ^[1] ; Marchesi, L. F. Q. P. ^[1] ; Forim, M. R. ^[1] ; Bulhoes, L. O. S. ^{[1, 2]} ; Pereira, E. C. ^[1] ; Santos, M. C. ^[3] ; Oliveira, R. T. S. ^[4]

Afiliação do(s) autor(es)

^[1] Univ Fed Sao Carlos, Dept Quim, BR-13565905 Sao Carlos, SP - Brazil

^[2] Ctr Univ Cent Paulista, CENIP, BR-13563470 Sao Carlos, SP - Brazil

^[3] Univ Fed ABC, LEMN, Ctr Ciencias Nat & Humanas, BR-09210170 Santo Andre, SP - Brazil

^[4] Univ Fed Triangulo Mineiro, Inst Ciencias Biol & Nat, BR-38025180 Uberaba, MG - Brazil

• Tipo de documento: Artigo Científico
• Fonte: Journal of the Brazilian Chemical Society; v. 22, n. 9, p. 1709-1717, SEP 2011.
• Citações Web of Science: 10

Resumo

This work describes a detailed study of the ethanol electrooxidation on Ti/(RuO(2))((x))Pt((1-x)) electrodes using several compositions prepared by the polymeric precursor method. The results obtained using cyclic voltammetry and chronoamperometry showed that the best composition of Ti/(RuO(2))((x))Pt((1-x)) electrodes for CO and ethanol oxidation processes is Ti/(RuO(2))(0.50)Pt(0.50). On this electrode composition the onset of CO and the ethanol oxidation occurred at 380 mV and 220 mV more negative than on Ti/Pt, respectively. Besides, there was an increase of 2.5-fold in the current density for ethanol electrooxidation under constant potential polarization. The Ti/(RuO(2))(0.50)Pt(0.50) electrodes produced lower amount of acetic acid compared to Ti/Pt and polycrystalline Pt electrodes using in situ HPLC spectrometric analysis. Also, a non common product from ethanol oxidation could be observed on higher RuO(2) loads: ethyl acetate. Finally, the impedance data showed that Ti/(RuO(2))(0.50)Pt(0.50) electrode composition had the smallest charge transfer resistance for ethanol oxidation among those compositions investigated. (AU)

• Processo FAPESP: 05/59992-6 - Materiais nanoestruturados: eletrocatálise e membranas de óxidos
• Beneficiário: Mauro Coelho dos Santos
• Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores
• Processo FAPESP: 10/05555-2 - Investigação da formação eletroquímica de nanotubos-TiO2 e sua aplicação em sistemas conversores de energia nanoarquiteturados
• Beneficiário: Renato Garcia de Freitas Sobrinho
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 03/09933-8 - Núcleo de Excelência em Materiais Nanoestruturados Fabricados Eletroquimicamente
• Beneficiário: Ernesto Chaves Pereira de Souza
• Modalidade de apoio: Auxílio à Pesquisa - Programa PRONEX - Temático