Greener preparation of a flexible material based on macaw palm oil derivatives and CO₂

Autor(es)

Alarcon, Rafael Turra ; Gaglieri, Caroline ; Bannach, Gilbert ; Cavalheiro, eder Tadeu Gomes

• Tipo de documento: Artigo Científico
• Fonte: GREEN CHEMISTRY; v. 26, n. 6, p. 10-pg., 2024-02-06.

Resumo

Carbonated macaw palm oil and maleinised macaw palm oil were reacted with five different amines to obtain renewable copolymers with a bio-based content greater than 80%. The polymerisation process is greener and reduces parallel reactions in the glycerol ester backbone. Polymerisation was completed in only 24 h at 120 C-degrees. Polymers demonstrated flexible properties and were in a rubbery state at room temperature. The polymer using 1,6-hexanediamine-HDA showed hydrophobicity and could be a promising coating for wood that can be used for industrial applications. Moreover, all polymers were totally hydrolysed in a sodium hydroxide solution. (AU)

• Processo FAPESP: 21/02152-9 - Síntese verde, caracterização e aplicação de novos biopolímeros a partir de óleos vegetais / essenciais usando-se compostos de enxofre como agentes intercruzantes
• Beneficiário: Gilbert Bannach
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 21/14879-0 - Novo método para síntese de polihidróxiuretanos a partir de triacilglicerol e utilizando catalisadores ou triacilmelamina, visando inibir reações paralelas
• Beneficiário: Rafael Turra Alarcon
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 22/15211-6 - Preparação e Aplicação de Eletrodos Compósitos à Base de Grafite e Polímeros: miniaturização, eletrodos impressos e sensores flexíveis
• Beneficiário: Éder Tadeu Gomes Cavalheiro
• Modalidade de apoio: Auxílio à Pesquisa - Regular