Er:YAl3(BO3)(4) glassy thin films from polymeric precursor and sol-gel methods: Waveguides for integrated optics

Autor(es)

Maia, L. J. Q. ^[1] ; Mastelaro, V. R. ^[2] ; Hernandes, A. C. ^[2] ; Fick, J. ^[3] ; Ibanez, A. ^[3]

Afiliação do(s) autor(es)

^[1] Univ Fed Goias, Inst Fis, BR-74001970 Goiania, Go - Brazil

^[2] Univ Sao Paulo, Inst Fis Sao Carlos, BR-13560970 Sao Carlos, SP - Brazil

^[3] Univ Grenoble 1, CNRS, Inst Neel, F-38042 Grenoble - France

• Tipo de documento: Artigo Científico
• Fonte: Thin Solid Films; v. 517, n. 24, p. 6584-6587, OCT 30 2009.
• Citações Web of Science: 15

Resumo

This paper presents the characterization of single-mode waveguides for 980 and 1550 nm wavelengths. High quality planar waveguide structure was fabricated from Y(1-x)Er(x)Al(3)(BO(3))(4) multilayer thin films with x = 0.02, 0.05, 0.1, 0.3, and 0.5, prepared through the polymeric precursor and sol-gel methods using spin-coating. The propagation losses of the planar waveguides varying from 0.63 to 0.88 dB/cm were measured at 632.8 and 1550 nm. The photoluminescence spectra and radiative lifetimes of the Er(3+) (4)I(13/2) energy level were measured in waveguiding geometry. For most samples the photoluminescence decay was single exponential with lifetimes in between 640 mu s and 200 mu s, depending on the erbium concentration and synthesis method. These results indicate that Er doped YAl(3)(BO(3))(4) compounds are promising for low loss waveguides. (C) 2009 Elsevier B.V. All fights reserved. (AU)