Surface agents' influence on the flexural strength of bilaminated ceramics

Texto completo
Autor(es):
Costa Lima, Julia Magalhaes [1] ; Anami, Lilian Costa [1] ; Rippe, Marilia Pivetta [1] ; de Melo, Renata Marques [2] ; Bottino, Marco Antonio [2] ; Valera, Marcia Carneiro [3] ; Maximo Araujo, Maria Amelia [3]
Número total de Autores: 7
Afiliação do(s) autor(es):
[1] UNESP, ICT, Grad Program Restorat, Sao Jose Dos Campos, SP - Brazil
[2] UNESP, Dept Dent Mat & Prosthodont, Inst Ciencia & Tecnol ICT, Sao Jose Dos Campos, SP - Brazil
[3] UNESP, Dept Restorat Dent, Inst Ciencia & Tecnol ICT, Sao Jose Dos Campos, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: Brazilian Oral Research; v. 27, n. 4, p. 311-317, Jul. 2013.
Citações Web of Science: 5
Resumo

The objective of this study was to evaluate the influence of different surface agents on the flexural strength of a ceramic system. Eighty bar-shaped specimens of zirconia were divided into four groups according to the agent to be used: group Control - to be cleaned with alcohol; group VM9 - application of a fluid layer of porcelain; group Effect Bonder - application of a bonding agent; and group Coloring Liquid - application of coloring liquid. All specimens received the porcelain application by the layering technique and were then subjected to thermocycling. The four-point bending test was performed to calculate the strength values (σ, MPa) and the failure modes were classified. ANOVA did not detect significant differences among the groups. The Weibull modulus were 5 (Control, VM9 and Effect Bonder) and 6 (Coloring Liquid). The cracking of the porcelain ceramic toward the interface was the predominant failure mode. It was concluded that the surface agents tested had no effect on the flexural strength of the bilaminated ceramic specimens. (AU)