Optical Properties and Surface morphology of ZnTe thin films prepared by multiple potential steps

Autor(es)

Murilo F. Gromboni ^[1] ; Francisco W. S. Lucas ^[1] ; Lucia H. Mascaro ^[1]

Afiliação do(s) autor(es)

^[1] Univ Fed Sao Carlos, Lab Eletroquim & Ceram LIEC, Dept Quim, BR-13565905 Sao Carlos, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: Journal of the Brazilian Chemical Society; v. 25, n. 3, p. 526-531, 2014-03-00.

Resumo

In this work, the ZnTe thin films were electrodeposited using potentiostatic steps, on Pt substrate. The effect of steps number, the deposition time for each element (Zn or Te) and layer order (Zn/Te or Te/Zn) in the morphology, composition, band gap energy and photocurrent was evaluated. Microanalysis data showed that the ratio Zn/Te ranged from 0.12 and 0.30 and the film was not stoichiometric. However, the band-gap value obtained from in all experimental conditions used in this work was 2.28 eV, indicating film growth of ZnTe. The samples with higher Zn showed higher photocurrent, which was of the order of 2.64 µA cm-2 and dendritic morphology. (AU)

• Processo FAPESP: 09/00788-1 - Obtenção e caracterização de filmes finos de ZnTe e ZnSe pela técnica de ECALE
• Beneficiário: Murilo Fernando Gromboni
• Modalidade de apoio: Bolsas no Brasil - Doutorado Direto
• Processo FAPESP: 12/10947-2 - Obtenção e caracterização de filmes finos de calcogenetos do tipo MBS (M = Ag ou Cu; B = In, Ga, Sb ou Tl; e S = S ou Se ) para aplicação em células fotovoltaicas
• Beneficiário: Francisco Willian de Souza Lucas
• Modalidade de apoio: Bolsas no Brasil - Doutorado
• Processo FAPESP: 10/18134-5 - Síntese eletroquímica e caracterização de filmes finos de Cd1-x ZnxTe, ZnSe e ZnTe
• Beneficiário: Lucia Helena Mascaro Sales
• Modalidade de apoio: Auxílio à Pesquisa - Regular