Effects of Er:YAG and Er,Cr:YSGG laser irradiation on the adhesion to eroded dentin

Autor(es)

Ramos, Thaysa Monteiro ^[1] ; Ramos-Oliveira, Thayanne Monteiro ^[1] ; de Freitas, Patricia Moreira ^[1] ; Azambuja, Jr., Nilton ^[1] ; Esteves-Oliveira, Marcella ^[2] ; Gutknecht, Norbert ^[2] ; Eduardo, Carlos de Paula ^[1]

Afiliação do(s) autor(es)

^[1] Univ Sao Paulo, Sch Dent, Dept Restorat Dent, Special Lab Lasers Dent LELO, BR-05508000 Sao Paulo - Brazil

^[2] Rhein Westfal TH Aachen, Dept Operat Dent Periodontol & Prevent Dent ZPP, D-52074 Aachen - Germany

• Tipo de documento: Artigo Científico
• Fonte: Lasers in Medical Science; v. 30, n. 1, p. 17-26, JAN 2015.
• Citações Web of Science: 12

Resumo

Limited information is available regarding the adhesion to eroded dentin. This study aims to evaluate the effect of different surface treatments on eroded dentin morphology and on microtensile bond strength (mu TBS) of adhesive systems to this substrate. Ninety-six extracted third molars were randomly divided into eight groups (n = 12) according to the type of surface treatment and the adhesive system: G1 = Control + Clearfil SE Bond {[}SE], G2 = Diamond bur {[}DB] + SE, G3 = Er:YAG laser (60 mJ, 2 Hz, 0.12 W, 19.3 J/ cm(2)) + SE, G4 = Er,Cr:YSGG laser (50 mJ, 30 Hz, 1.5 W, 4.5 J/ cm(2)) + SE, G5 = Control + Single Bond {[}SB], G6 = DB + SB, G7 = Er:YAG + SB, G8 = Er,Cr:YSGG + SB. The erosive cycling was performed by immersion in 0.05 M citric acid (pH 2.3, 10 min, 6x/day) and in supersaturated solution (pH 7.0, 1 h, between acid attacks), during 5 days. Blocks of composite were bonded to the samples according to the manufacturers' instructions. After 24 h-storage in distilled/deionized water (37 A degrees C), stick-shaped samples were obtained and submitted to mu TBS test. Each surface treatment was analyzed under scanning electron microscopy (n = 4) and the bond strength values (megapascal) were analyzed by two-way ANOVA and Tukey tests (alpha = 0.05). All surface treatments lead to changes on eroded dentin. G4 showed the highest bond strength mean (28.3 A +/- 9.2 MPa), which was statistically significant higher than all the other groups (p < 0.05). The surface treatment with Er,Cr:YSGG laser irradiation (4.5 J/cm(2)/50 mJ/30 Hz/140 mu s) prior to bonding with a self-etching adhesive system significantly increases adhesion to eroded dentin, as compared to conventional treatment. (AU)

• Processo FAPESP: 11/02925-6 - Estudo in vitro da morfologia e da resistência adesiva da resina à dentina humana irradiada com laser de Er:YAG e submetida ao desafio erosivo