Antiferromagnetism induced by oxygen vacancies in V2O5 polycrystals synthesized by the Pechini method

Texto completo
Autor(es):
Dreifus, D. [1] ; Godoy, M. P. F. [1] ; Rabelo, A. C. [2] ; Rodrigues, A. D. [1] ; Gobato, Y. G. [1] ; Camargo, P. C. [1] ; Pereira, E. C. [2] ; de Oliveira, A. J. A. [1]
Número total de Autores: 8
Afiliação do(s) autor(es):
[1] Univ Fed Sao Carlos UFSCar, Dept Fis, Sao Carlos, SP - Brazil
[2] Univ Fed Sao Carlos UFSCar, Dept Quim, Sao Carlos, SP - Brazil
Número total de Afiliações: 2
Tipo de documento: Artigo Científico
Fonte: JOURNAL OF PHYSICS D-APPLIED PHYSICS; v. 48, n. 44 NOV 11 2015.
Citações Web of Science: 0
Resumo

Optical and magnetic properties of V2O5 polycrystals were investigated through photoluminescence (PL) and magnetization measurements. The PL spectra comprise two main bands attributed to oxygen vacancies and to band-edge-related transitions. The magnetization measurements showed a predominant paramagnetic behavior in the temperature range studied (5 K-300 K) with a superimposed peak around 80 K associated with an antiferromagnetic phase. The temperature dependence of the magnetic results and the relative PL intensity presented a remarkable correlation while in the range of 80-200 K the intensity associated with oxygen vacancies became considerably more intense than band-to-band emissions, the same range in which the antiferromagnetic transition was observed. The observation of an antiferromagnetic phase in V2O5 was predicted in the literature although this result had not previously been measured experimentally. Raman spectroscopy was used as a complementary technique in order to exclude the presence of spurious vanadium oxide phases in the sample. (AU)

Processo FAPESP: 13/17657-2 - Síntese e propriedades ópticas de sistemas semicondutores para aplicação em spintrônica
Beneficiário:Marcio Peron Franco de Godoy
Linha de fomento: Auxílio à Pesquisa - Regular
Processo FAPESP: 12/24025-0 - Propriedades magnética, elétrica e magnetostrictiva de compósitos multiferróicos e óxidos semicondutores magnéticos diluídos
Beneficiário:Adilson Jesus Aparecido de Oliveira
Linha de fomento: Auxílio à Pesquisa - Regular
Processo FAPESP: 13/07296-2 - CDMF - Centro de Desenvolvimento de Materiais Funcionais
Beneficiário:Elson Longo da Silva
Linha de fomento: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs