Residual sisal fibers treated by methane cold plasma discharge for potential application in cement based material

Texto completo
Autor(es):
Barra, B. N. [1] ; Santos, S. F. [2] ; Bergo, P. V. A. [1] ; Alves, Jr., C. [3] ; Ghavami, K. [4] ; Savastano, Jr., H. [1]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Univ Sao Paulo, Dept Engn Biossistemas, Pirassununga, SP - Brazil
[2] Univ Estadual Paulista UNESP, Dept Mat & Tecnol, Guaratingueta, SP - Brazil
[3] Univ Fed Rural Semiarido UFERSA, CiTED Ctr Integrado Inovacao Tecnol Semiarido, Mossoro, RN - Brazil
[4] Pontificia Univ Catolica Rio de Janeiro PUC RJ, Dept Engn Civil, Rio De Janeiro, RJ - Brazil
Número total de Afiliações: 4
Tipo de documento: Artigo Científico
Fonte: INDUSTRIAL CROPS AND PRODUCTS; v. 77, p. 691-702, DEC 23 2015.
Citações Web of Science: 15
Resumo

The use of residual sisal fiber is becoming more frequent as reinforcement element in organic or inorganic matrix due to its low cost, high abundance in some countries and constitutes a renewable material. However, a significant loss in the mechanical performance in long term has been observed in fiber-cement composites after natural aging. These alternative fibers can be utilized in a hybrid fiber-cement in order to decrease the content of traditionally used synthetic fibers. The objective of this work was to evaluate the potential of the methane cold plasma treatment of 10 min duration on structural and physical properties of the residual sisal fibers to mitigate the degradation mechanisms when applied to cementitious matrices. Moisture sensitivity evaluation by capacitance method, dielectric measurements, X-ray diffraction, Fourier transform infrared (FTIR), spectroscopy, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), atomic force microscopy (AFM), angle contact and pullout test were carried out in order to follow the effect of the proposed treatment. Besides, mechanical behavior of untreated and treated sisal fibers was evaluated before and after accelerated aging in cementitious solution at 60 degrees C by 72 h. The results obtained in all these tests confirmed the high potential of the methane cold plasma treatment to delay the degradation of the residual sisal fibers in the presence of a Portland cement environment and these fibers present the higher pullout load and shear stress than one untreated. (C) 2015 Published by Elsevier B.V. (AU)

Processo FAPESP: 09/10614-0 - Características mecânicas fundamentais de compósitos não convencionais com reforço de fibras celulósicas e sintéticas: contribuição para materiais construtivos sustentáveis
Beneficiário:Holmer Savastano Junior
Linha de fomento: Auxílio à Pesquisa - Regular
Processo FAPESP: 09/17293-5 - Mecânica da fratura aplicada ao desenvolvimento de compósitos não convencionais extrudados com reforço de fibras celulósicas e sintéticas
Beneficiário:Sérgio Francisco dos Santos
Linha de fomento: Auxílio à Pesquisa - Apoio a Jovens Pesquisadores
Processo FAPESP: 10/16524-0 - Mecânica da fratura aplicada ao desenvolvimento de compósitos não convencionais extrudados com reforço de fibras celulósicas e sintéticas
Beneficiário:Sérgio Francisco dos Santos
Linha de fomento: Bolsas no Brasil - Apoio a Jovens Pesquisadores
Processo FAPESP: 08/04769-9 - Estudo da degradação de fibras celulósicas em compósitos cimentícios: contribuição para materiais construtivos sustentáveis
Beneficiário:Alessandra Etuko Feuzicana de Souza Almeida
Linha de fomento: Bolsas no Brasil - Pós-Doutorado