Interface formation and properties of friction spot welded joints of AA5754 and Ti6Al4V alloys

Texto completo
Autor(es):
Plaine, A. H. [1, 2] ; Suhuddin, U. F. H. [1] ; Afonso, C. R. M. [2] ; Alcantara, N. G. [2] ; dos Santos, J. F. [1]
Número total de Autores: 5
Afiliação do(s) autor(es):
[1] Helmholtz Zentrum Geesthacht, Inst Mat Res, Mat Mech, Solid State Joining Proc, Max Planck Str 1, D-21502 Geesthacht - Germany
[2] Univ Fed Sao Carlos, Dept Mat Engn, R Washington Luis Km 235, BR-310 Sao Carlos, SP - Brazil
Número total de Afiliações: 2
Tipo de documento: Artigo Científico
Fonte: MATERIALS & DESIGN; v. 93, p. 224-231, MAR 5 2016.
Citações Web of Science: 11
Resumo

This study aims to understand the influence of dwell time on the microstructure of the interface and lap shear strength of friction spot welded joints of AA5754 and Ti6Al4V alloys. The interface reaction layer consists mainly of TiAl3 intermetallic compound. It was noticed that dwell time significantly influences the diffusion process during the friction spot welding, thereby modifying the thickness of the interface and thus affecting the mechanical performance of the joints. Minimizing or optimizing the brittle TiAl3 phase was demonstrated to be the key issue to achieve high strength Ti/Al dissimilar joints. The intermetallic compound growth kinetics was also examined showing that an incubation time of approximately 2.7 s is necessary before it nucleates at the Ti/Al interface and grows laterally to form a continuous layer. Afterwards, the TiAl3 layer grows toward the Al during thickening with a corresponding growth rate of k = 2.92 x 10(-7) m/s. These results are critical to understand the microstructure-properties relationship and contribute with additional improvements on the joint performance. (C) 2015 Elsevier Ltd. All rights reserved. (AU)