Busca avançada
Ano de início
Entree
(Referência obtida automaticamente do SciELO, por meio da informação sobre o financiamento pela FAPESP e o número do processo correspondente, incluída na publicação pelos autores.)

Reliability of FEA on the Results of Mechanical Properties of Materials

Texto completo
Autor(es):
Erica Alves Gomes [1] ; Hugo Henrique Diana [2] ; Juliana Santos Oliveira [3] ; Yara Teresinha Corrêa Silva-Sousa [4] ; Adriana Cláudia Lapria Faria [5] ; Ricardo Faria Ribeiro [6]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] UNAERP - Universidade de Ribeirão Preto. Dental School - Brasil
[2] UNAERP - Universidade de Ribeirão Preto. Dental School - Brasil
[3] UNAERP - Universidade de Ribeirão Preto. Dental School - Brasil
[4] UNAERP - Universidade de Ribeirão Preto. Dental School - Brasil
[5] USP - Universidade de São Paulo. School of Dentistry of Ribeirão Preto. Department of Dental Materials and Prosthodontics - Brasil
[6] USP - Universidade de São Paulo. School of Dentistry of Ribeirão Preto. Department of Dental Materials and Prosthodontics - Brasil
Número total de Afiliações: 6
Tipo de documento: Artigo Científico
Fonte: Brazilian Dental Journal; v. 26, n. 6, p. 667-670, 2015-12-00.
Resumo

The present study evaluated the reliability of FEA on the results of different mechanical properties (E and v) of materials. Two 3D models of a maxillary canine with endodontic treatment, intracanal post, composite resin core and restored with porcelain-fused-to-metal crown were generated according to micro-CT images. Two groups with different E and ν values for porcelain, metal coping alloy, resin cement and composite resin were established. The materials' properties for group GL were based on literature data, while for group GIE the impulse excitation technique was used. A load of 180 N was applied at 45° on the incisal third of the lingual surface of the canine tooth. All models were supported by the periodontal ligament (x=y=z=0). The von Mises stress (VMS) was calculated. The stress values revealed differences between the groups for both VMS distribution and value. The porcelain (GL: 5.966 MPa; GIE: 7.478 MPa), metal coping (GL: 3.811 MPa; GIE: 0.973 MPa) and core (GL: 4.771 MPa; GIE: 0.026 MPa) were significantly affected. In conclusion, this study showed that the determination of mechanical properties (E and ν) of materials is essential for the reliability on the results of FEA. (AU)

Processo FAPESP: 13/23905-9 - Distribuição de tensões em raízes reabilitadas com pinos de fibra e um pino experimental de dentina: uma análise pelo MEF-3D