High Nd3+Yb3+ energy transfer efficiency in tungsten-tellurite glass: A promising converter for solar cells

Autor(es)

Costa, Francine Bettio ; Yukimitu, Keizo ; de Oliveira Nunes, Luiz Antonio ; Figueiredo, Marcio da Silva ; Silva, Junior Reis ; da Cunha Andrade, Luis Humberto ; Lima, Sandro Marcio ; Silos Moraes, Joao Carlos

• Tipo de documento: Artigo Científico
• Fonte: Journal of the American Ceramic Society; v. 100, n. 5, p. 1956-1962, MAY 2017.
• Citações Web of Science: 8

Resumo

This work reports on the energy transfer efficiency for Nd3+/Yb3+ co-doped tellurite glasses (80TO(2)-20WO(3), in mol%,). The correlation between Yb3+ ion concentration and the downconversion mechanism was investigated using optical and thermal lens spectroscopies, which enabled investigation of the radiative and nonradiative processes, respectively, involved in energy transfer from neodymium to ytterbium. The Nd3+ near-infrared fluorescence disappeared almost entirely when the maximum concentration of Yb3+ ions (4mol%) was doped into the host. In contrast, there was a corresponding increase in the ytterbium emission at around 980nm. When ytterbium was added, there was also a simultaneous reduction in the amount of heat generated by the sample due to a reduction in the nonradiative decay rate, corroborating the suspected high energy transfer efficiency of Nd3+Yb3+. The results indicate that tungsten-tellurite glasses may be of potential use in solar cells for matching the solar emission spectrum to the semiconductor cell. (AU)

• Processo FAPESP: 13/19747-9 - Investigação de propriedades espectroscópicas em vidros telúritos livres de OH-
• Beneficiário: João Carlos Silos Moraes
• Modalidade de apoio: Auxílio à Pesquisa - Regular