Resin composite repair for implant-supported crowns

Texto completo
Autor(es):
Bonfante, Estevam A. ; Suzuki, Marcelo ; Hirata, Ronaldo ; Bonfante, Gerson ; Fardin, Vinicius P. ; Coelho, Paulo G.
Número total de Autores: 6
Tipo de documento: Artigo Científico
Fonte: JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS; v. 105, n. 6, p. 1481-1489, AUG 2017.
Citações Web of Science: 1
Resumo

This study evaluated the reliability of implant-supported crowns repaired with resin composites. Fifty-four titanium abutments were divided in three groups (n = 18 each) to support resin nanoceramic molar crowns, as follows: (LU) (Lava Ultimate, 3M ESPE); LU repaired with either a direct or an indirect resin composite. Samples were subjected to mouth-motion accelerated-life testing in water (n 5 18). Cumulative damage with a use stress of 300 N was used to plot Weibull curves for group comparison. Reliability was calculated for a mission of 100,000 cycles at 400 N load. Beta values were 0.83 for LU, 0.31 and 0.27 for LU repaired with Filtek and Ceramage, respectively. Weibull modulus for LU was 9.5 and eta = 1047 N, m = 6.85, and eta = 1002 N for LU repaired with Ceramage, and m = 4.65 and eta = 766 N for LU repaired with Filtek (p < 0.10 between LU and LU repaired with Filtek). Reliability at 400 N was 100% for both LU and LU repaired with Ceramage which were significantly higher than LU Filtek repair (32%). LU restored crowns failed cohesively. Fractures were confined within the restored material, and detailed fractography is presented. The performance of resin nanoceramic material repaired with an indirect composite was maintained after accelerated-life testing compared to unrepaired controls. (C) 2016 Wiley Periodicals, Inc. (AU)

Processo FAPESP: 14/22859-6 - Efeito do desenho de infraestruturas de próteses parciais fixas de zircônia fadigadas quanto as propriedades nanomecânicas
Beneficiário:Vinicius Pavesi Fardin
Modalidade de apoio: Bolsas no Exterior - Estágio de Pesquisa - Doutorado
Processo FAPESP: 10/06152-9 - Confiabilidade e modos de fratura de próteses fixas em compósitos indiretos com e sem infra-estrutura CAD/CAM sobre implantes
Beneficiário:Estevam Augusto Bonfante
Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
Processo FAPESP: 13/20806-0 - Avaliação dos danos e modo de falha de próteses parciais fixas totalmente cerâmicas em função da aplicação de carga na crista marginal
Beneficiário:Vinicius Pavesi Fardin
Modalidade de apoio: Bolsas no Brasil - Doutorado