Enhancement of spectroscopic and luminescence properties of Er3+ doped tellurite glasses by adding P2O5 for lasing materials

Texto completo
Autor(es):
Jlassi, I. [1, 2] ; Fares, H. [3] ; Elhouichet, H. [1, 2]
Número total de Autores: 3
Afiliação do(s) autor(es):
[1] Ctr Natl Rech Sci Mat, Lab Physicochim Mat Mineraux & Leurs Applicat, BP. 95, Hammam Lif 2050 - Tunisia
[2] Univ Tunis El Manar, Fac Sci Tunis, Dept Phys, Campus Univ Farhat Hachad, Elmanar 2092 - Tunisia
[3] Sao Paulo State Univ, UNESP, Inst Chem, POB 355, BR-14801970 Araraquara, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: Journal of Luminescence; v. 194, p. 569-578, FEB 2018.
Citações Web of Science: 7
Resumo

Er3+-doped phosphor-tellurite glasses has been synthesized by conventional melting method. Results of differential scanning calorimetry (DSC) measurements indicate a good thermal stability of tellurite glasses. The DSC measurements show an improvement of thermal stability of glass hosts after adding P2O5. The structures of glasses were investigated by X-ray diffraction (XRD) and Raman spectroscopy to understand their dependence of structure on composition. Absorption spectrum from near infrared to visible was obtained and the JuddOfelt (J-O) intensity parameters (Omega(2), Omega(4), and Omega(6)) were determined. Spontaneous emission probabilities of some relevant transitions, branching ratio, and radiative lifetimes of several excited states of Er3+ have been predicted using intensity J-O parameters. Up-conversion luminescence characteristics, under 977 nm excitation wavelength, have been investigated at room and low temperature in these glasses. Intense green and red emissions from Er3+ centered at 534 nm, 548 nm and 660 nm, corresponding to the transitions H-2(11/2)-> I-4(15/2), S-4(3/2)-> I-4(15/2) and F-4(9/2)-> I-4(15/2), respectively, were simultaneously observed. The quadratic dependence of the up-conversion emission on the excitation power indicates that two-photon steps are involved for the three visible emission bands. The PL lifetimes is found to decrease in the temperature range 77-300 K. Using the Mc-Cumber method, emission cross-section (sigma(e)), Absorption cross-section (sigma(a)), and gain cross-section (G(lambda)) for the I-4(13/2)-> I-4(15/2) transition, were calculated. By analyzing obtained data based to all advantages after adding P2O5, the tellurite glasses can be used as potential host material for developing optical amplifiers applied for 1.53 mu m band broad and high-gain erbium-doped fiber amplifiers (EDFA). (AU)

Processo FAPESP: 16/16343-2 - Síntese e caracterização de vidros e vitrocerâmicas transparentes contendo íons terras raras
Beneficiário:Hssen Fares
Linha de fomento: Bolsas no Brasil - Pós-Doutorado
Processo FAPESP: 13/07793-6 - CEPIV - Centro de Ensino, Pesquisa e Inovação em Vidros
Beneficiário:Edgar Dutra Zanotto
Linha de fomento: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs