Water interaction and bond strength to dentin of dye-labelled adhesive as a function of the addition of rhodamine B

Autor(es)

Linda WANG ^[1] ; Odair BIM JÚNIOR ^[2] ; Adolfo Coelho de Oliveira LOPES ^[3] ; Luciana Fávaro FRANCISCONI-DOS-RIOS ^[4] ; Rafael Massunari MAENOSONO ^[5] ; Paulo Henrique Perlatti DALPINO ^[6] ; Heitor Marques HONÓRIO ^[7] ; Maria Teresa ATTA ^[8]

Afiliação do(s) autor(es)

^[1] Universidade de São Paulo. Faculdade de Odontologia de Bauru. Departamento de Dentística, Endodontia e Materiais Odontológicos - Brasil

^[2] Universidade de São Paulo. Faculdade de Odontologia de Bauru. Departamento de Dentística, Endodontia e Materiais Odontológicos - Brasil

^[3] Universidade de São Paulo. Hospital de Reabilitação de Anomalias Craniofaciais - Brasil

^[4] Universidade de São Paulo. Faculdade de Odontologia. Departamento de Dentística - Brasil

^[5] Universidade de São Paulo. Faculdade de Odontologia de Bauru. Departamento de Dentística, Endodontia e Materiais Odontológicos - Brasil

^[6] Universidade Anhanguera-Bandeirantes - Brasil

^[7] Universidade de São Paulo. Faculdade de Odontologia de Bauru. Departamento de Odontopediatria, Ortodontia e Saúde Coletiva - Brasil

^[8] Universidade de São Paulo. Faculdade de Odontologia de Bauru. Departamento de Dentística, Endodontia e Materiais Odontológicos - Brasil

• Tipo de documento: Artigo Científico
• Fonte: Journal of Applied Oral Science; v. 24, n. 4, p. 317-324, 2016-08-00.

Resumo

ABSTRACT Objective This study investigated the effect of the fluorescent dye rhodamine B (RB) for interfacial micromorphology analysis of dental composite restorations on water sorption/solubility (WS/WSL) and microtensile bond strength to dentin (µTBS) of a 3-step total etch and a 2-step self-etch adhesive system. Material and Methods The adhesives Adper Scotchbond Multi-Purpose (MP) and Clearfil SE Bond (SE) were mixed with 0.1 mg/mL of RB. For the WS/WSL tests, cured resin disks (5.0 mm in diameter x 0.8 mm thick) were prepared and assigned into four groups (n=10): MP, MP-RB, SE, and SE-RB. For µTBS assessment, extracted human third molars (n=40) had the flat occlusal dentin prepared and assigned into the same experimental groups (n=10). After the bonding and restoration procedures, specimens were sectioned in rectangular beams, stored in water and tested after seven days or after 12 months. The failure mode of fractured specimens was qualitatively evaluated under optical microscope (x40). Data from WS/WSL and µTBS were assessed by one-way and three-way ANOVA, respectively, and Tukey’s test (α=5%). Results RB increased the WSL of MP and SE. On the other hand, WS of both MP and SE was not affected by the addition of RB. No significance in µTBS between MP and MP-RB for seven days or one year was observed, whereas for SE a decrease in the µTBS means occurred in both storage times. Conclusions RB should be incorporated into non-simplified DBSs with caution, as it can interfere with their physical-mechanical properties, leading to a possible misinterpretation of bonded interface. (AU)

• Processo FAPESP: 12/13160-3 - Efeito de adição de agente fluorescente (Rodamina B) a sistemas adesivos não simplificados: análise de propriedades físico-mecânicas
• Beneficiário: Linda Wang
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 11/14971-2 - Avaliação do efeito de adição de agente fluorescente (Rodamina B) a sistemas adesivos não simplificados.
• Beneficiário: Odair Bim Júnior
• Modalidade de apoio: Bolsas no Brasil - Mestrado