Morphology of Electrospun Non-Woven Membranes of Poly(vinylidene fluoride-co-hexafluoropropylene): Porous and Fibers

Texto completo
Autor(es):
Dognani, Guilherme [1] ; Cabrera, Flavio Camargo [1] ; Job, Aldo Eloizo [1] ; da Silva Agostini, Deuber Lincon [1]
Número total de Autores: 4
Afiliação do(s) autor(es):
[1] Sao Paulo State Univ FCT UNESP, Sch Technol & Sci, BR-19060080 Presidente Prudente - Brazil
Número total de Afiliações: 1
Tipo de documento: Artigo Científico
Fonte: FIBERS AND POLYMERS; v. 20, n. 3, p. 512-519, MAR 2019.
Citações Web of Science: 0
Resumo

In this paper, poly(vinylidene fluoride-co-hexafluoropropylene) nanofibers membranes were fabricated by facile single-capillary electrospinning at different times of production. The materials were characterized by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), atomic force microscopy (AFM), contact angle (CA), mercury porosity intrusion (MIP), Tensile tests, capillary flow porosity (CFP) and, BET surface by nitrogen adsorption-desorption. The membranes were fabricated varying the fibers density, the thickness and the morphology. The samples presented a good fiber diameter distribution and an average diameter of 321 nm. AFM results showed high porosity (82.7-87.5 %), a high contact angle of 159.2 degrees, mean pore size of 0.637 m and hydrophobicity of the membranes. A low value of permeate pure water flux, 5.2 %, was observed for the densest fabricated membrane. The porosity of fibers diameters was similar for all samples, which is an important parameter as they can be potential materials for membrane distillation process. (AU)

Processo FAPESP: 16/06288-4 - Desenvolvimento de nanofibras polímericas condutoras obtidas por eletrofiação para aplicação em sensores e heterojunções
Beneficiário:Deuber Lincon da Silva Agostini
Linha de fomento: Auxílio à Pesquisa - Regular
Processo FAPESP: 15/21261-2 - Desenvolvimento de pré-filtros de água a partir de membranas eletrofiadas de PVDF com superfície funcionalizada para adsorção do CR6+
Beneficiário:Guilherme Dognani
Linha de fomento: Bolsas no Brasil - Doutorado