Impact of calcium aluminate cement with additives on dental pulp-derived cells

Texto completo
Autor(es):
Nadyne Saab Messias [1] ; Gabriela Grisote [2] ; Antonio Secco Martorano [3] ; Roger Rodrigo Fernandes [4] ; Ivone Regina de Oliveira [5] ; Karina Fittipaldi Bombonato-Prado [6] ; Paulo Tambasco de Oliveira [7] ; Larissa Moreira Spinola de Castro-Raucci [8]
Número total de Autores: 8
Afiliação do(s) autor(es):
[1] Universidade de Ribeirão Preto. Faculdade de Odontologia - Brasil
[2] Universidade de Ribeirão Preto. Faculdade de Odontologia - Brasil
[3] Universidade de Ribeirão Preto. Faculdade de Odontologia - Brasil
[4] Universidade de São Paulo. Faculdade de Odontologia de Ribeirão Preto - Brasil
[5] Universidade do Vale do Paraíba. Instituto de Pesquisa e Desenvolvimento - Brasil
[6] Universidade de Ribeirão Preto. Faculdade de Odontologia - Brasil
[7] Universidade de São Paulo. Faculdade de Odontologia de Ribeirão Preto - Brasil
[8] Universidade de Ribeirão Preto. Faculdade de Odontologia - Brasil
Número total de Afiliações: 8
Tipo de documento: Artigo Científico
Fonte: Journal of Applied Oral Science; v. 28, 2019-11-28.
Resumo

Abstract Calcium aluminate cement (CAC) has been highlighted as a promising alternative for endodontic use aiming at periapical tissue repair. However, its effects on dental pulp cells have been poorly explored. Objective: This study assessed the impact of calcium chloride (CaCl2) and bismuth oxide (Bi2O3) or zinc oxide (ZnO) additives on odontoblast cell response to CAC. Methodology: MDPC-23 cells were exposed for up to 14 d: 1) CAC with 2.8% CaCl2 and 25% ZnO (CACz); 2) CAC with 2.8% CaCl2 and 25% Bi2O3 (CACb); 3) CAC with 10% CaCl2 and 25% Bi2O3 (CACb+); or 4) mineral trioxide aggregate (MTA), placed on inserts. Non-exposed cultures served as control. Cell morphology, cell viability, gene expression of alkaline phosphatase (ALP), bone sialoprotein (BSP), and dentin matrix protein 1 (DMP-1), ALP activity, and extracellular matrix mineralization were evaluated. Data were compared using ANOVA (α=5%). Results: Lower cell density was detected only for MTA and CACb+ compared with Control, with areas showing reduced cell spreading. Cell viability was similar among groups at days one and three (p>0.05). CACb+ and MTA showed the lowest cell viability values at day seven (p>0.05). CACb and CACb+ promoted higher ALP and BSP expression compared with CACz (p<0.05); despite that, all cements supported ALP activity. Matrix mineralization were enhanced in CACb+ and MTA. Conclusion: In conclusion, CAC with Bi2O3, but not with ZnO, supported the expression of odontoblastic phenotype, but only the composition with 10% CaCl2 promoted mineralized matrix formation, rendering it suitable for dentin-pulp complex repair. (AU)

Processo FAPESP: 16/11461-7 - Resposta de células da linhagem odontoblástica a diferentes preparações de cimento de aluminato de cálcio
Beneficiário:Nadyne Saab Messias
Modalidade de apoio: Bolsas no Brasil - Iniciação Científica
Processo FAPESP: 10/50936-4 - Efeitos de diferentes preparações de cimento de aluminato de cálcio sobre culturas de células osteogênicas e de células indiferenciadas da polpa dental
Beneficiário:Paulo Tambasco de Oliveira
Modalidade de apoio: Auxílio à Pesquisa - Regular