Yb3+/Er(3+)co-doped Dion-Jacobson niobium layered perovskites as NIR-to-green upconversion materials

Autor(es)

Vendruscolo, Victor ^[1] ; Giordano, Luidgi ^[1] ; Leopoldo Constantino, Vera Regina ^[1] ; Veloso Rodrigues, Lucas Carvalho ^[1]

Afiliação do(s) autor(es)

^[1] Univ Sao Paulo, Inst Chem, Dept Fundamental Chem, Av Prof Lineu Prestes 748, BR-05508000 Sao Paulo, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: NEW JOURNAL OF CHEMISTRY; v. 44, n. 24, p. 10165-10171, JUN 28 2020.
• Citações Web of Science: 0

Resumo

Here, the upconversion behaviour of Yb3+/Er3+-codoped layered Dion-Jacobson calcium-niobium perovskites was investigated. This lanthanide pair is majorly responsible for the efficient green and red anti-Stokes-like emissions in rare-earth fluorides. Layered perovskites of the composition KCa(2)Nb(3)O(10)were synthesized by the ceramic method by replacing 1% per mol of Ca(2+)by lanthanide ions in such a way that the Yb3+:Er(3+)molar proportion varied from 2 : 1 to 20 : 1. Non-doped and four doped materials were characterized by X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy (SEM), and emission spectroscopy. All materials showed similar XRD profiles, which indicated the isolation of well crystalline single phases. On the other hand, the morphologies accessed by SEM were different: microparticles with well-defined edges were replaced by particles with poorly defined edges, rounded features, and intergrowth aspect when the niobate was doped. The Raman spectra showed modifications in the bands below 200 cm(-1)attributed to low-phonon-energy transitions. The doped layered niobates presented almost pure-green emission (excitation at 980 nm), which could be related to the low energy values of the vibrational levels, precluding energy loss. Additionally, the results indicated that the defects generated by the lanthanide ion isomorphic-aliovalent substitution in Ca(2+)sites were mainly in the interlayer region. This coupled behaviour reduced the non-radiative decays of the upconversion centres, leading to the formation of an efficient emitting material. The spectroscopic emission data showed a two-photon major mechanism to excite the emitting levelsviaan energy transfer upconversion (ETU) population process. The lifetime results indicated that increasing the Yb(3+)concentration did not lead to non-radiative decay paths. The high efficiency and the versatility of the layered niobate hosts can provide new insights into the design of efficient morphology-controlled materials. (AU)

• Processo FAPESP: 18/05280-5 - Materiais fotônicos ativos no vermelho-infravermelho para conversão e armazenamento de energia
• Beneficiário: Lucas Carvalho Veloso Rodrigues
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 14/50869-6 - INCT 2014: em Eletrônica Orgânica INEO
• Beneficiário: Roberto Mendonça Faria
• Modalidade de apoio: Auxílio à Pesquisa - Temático