XPS analysis of bridging and non-bridging oxygen in Yb3+-Er3+-Tm3+-doped zinc-tellurite glasses

Autor(es)

Clabel, J. L. H. ^[1] ; Lozano, G. ^[1] ; Marega Jr, E. ; Rivera, V. A. G. ^[2]

Afiliação do(s) autor(es)

^[1] Univ Sao Paulo, Inst Fis Sao Carlos, Caixa Postal 369, BR-13560970 Sao Carlos, SP - Brazil

^[2] Univ Nacl Mayor San Marcos UNMSM, Fac Ciencias Fis, Lima - Peru

• Tipo de documento: Artigo Científico
• Fonte: Journal of Non-Crystalline Solids; v. 553, FEB 1 2021.
• Citações Web of Science: 2

Resumo

Influence of Er3+, Yb3+ and Tm3+ on the network structure of zinc-tellurite glasses is investigated by refraction index and high-resolution X-ray photoelectron spectroscopy (XPS) in order to clarify the role of rare-earth ions in the formation of non-bridging and bridging oxygens (NBO and BO, respectively). The NBO atoms were responsible for high polarizability, as confirmed from the correlations between the local structure and polarizability, where have been tentatively established high linear fit r(2) =0.96 and 0.98 when the excitation wavelengths are 532 and 632.8 nm, respectively. The structural origin of the NBO atoms into the zinc-tellurites glasses is discussed by analysis of the component number from the deconvolution in the XPS spectra. In this analysis, Te 3d peaks shift by about 0.23 eV towards higher binding energy from TZ1 to TZ4, and spin-orbit splitting between Te 3d(5/2) and Te 3d(3/2) to all glasses remain unchanged, Delta E approximate to 10.4 eV. While Zn 2p peaks shift by about 1.08, eV towards higher binding energy, and spin-orbit splitting between Zn 2p(3/2) and Zn 2p(1/2) increase of 23.08 eV (TZ1 to TZ3) to 24.09 eV (TZ4) whit the increase REI. The O 1s spectra suggest that the increase of REI concentration produces additional environments for REI with bonds through lone-pair electrons, favoring the formation of NBOs. It was observed that the increasing the concentrations of REI has a high linear dependence with increased of NBO atoms in the glass network, r(2) =0.87. (AU)

• Processo FAPESP: 13/07276-1 - CEPOF - Centro de Pesquisa em Óptica e Fotônica
• Beneficiário: Vanderlei Salvador Bagnato
• Modalidade de apoio: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs