Cryogenic- and ultrasonic-induced local martensite-like order in Cu47.5Zr45.5Al5Er2 bulk metallic glasses

Texto completo
Autor(es):
Moreno-Gobbi, A. [1] ; Silva Jr, P. S. ; Maso, A. [1] ; Marques, P. W. B. [2] ; Florencio, O. [2, 3] ; Sarasua, L. G. [1]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Inst Fis, Fac Ciencias UDELAR, Igua 4225, Montevideo 11400 - Uruguay
[2] Silva Jr, Jr., P. S., Univ Fed Sao Carlos, Dept Phys, BR-13565905 Sao Carlos, SP - Brazil
[3] Univ Prebiteriana Mackenzie, Engn Sch, BR-01302907 Sao Paulo, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: MATERIALS TODAY COMMUNICATIONS; v. 26, MAR 2021.
Citações Web of Science: 0
Resumo

This study analyzed the influence of low-temperature elastic ultrasonic stimulus on the local structural order of Cu47.5Zr45.5Al5Er2 amorphous alloy, using the ultrasonic pulse-echo technique with a longitudinal wave frequency of 10 MHz, between 100 K-300 K under consecutive cryogenic thermal cycles. Ultrasonic attenuation and wave velocity data of Cu47.5Zr45.5Al5Er2 sample revealed an evolution of the anomalies observed between cooling and heating cycles, being the progressive changes in the local amorphous structure related to the forming and grown of the locally ordered structures induced by the consecutive cryogenic and ultrasonic waves cycles. After the Cu47.5Zr45.5Al5Er2 sample maintained free of mechanical stress at RT for a week, their anelastic response exhibited the full recovery of the as-received condition ultrasonic behavior, denoting the metastable nature of the short- and medium-range order structures originated from the thermomechanical cycles. The amorphous sample ultrasonic response showed attenuation peaks compatible with those observed in a Cu36Zr59Al5 crystalline sample, ass-ociated with a typical reversible martensitic transformation between B2 CuZr to B19' and B33 CuZr phases. (AU)

Processo FAPESP: 13/13378-1 - Relaxações Anelásticas na Identificação de Processos de Migração Atômica e Rearranjo Estrutural em Ligas Metálicas com Alta Tendência à Formação de Vidro (Ligas Vítreas e Nanocristalinas)
Beneficiário:Paulo Wilmar Barbosa Marques
Linha de fomento: Bolsas no Brasil - Pós-Doutorado
Processo FAPESP: 17/09715-3 - Relaxações Anelásticas na Identificação de Processos de Rearranjo Estrutural e Transições de Fase em Compósitos Metálicos Amorfos com Memória de Forma
Beneficiário:Paulo Wilmar Barbosa Marques
Linha de fomento: Bolsas no Brasil - Pós-Doutorado