Additively manufactured carbon/black-integrated polylactic acid 3Dprintedsensor for simultaneous quantification of uric acid and zinc in sweat

Autor(es)

Ataide, Vanessa N. ^[1] ; Rocha, Diego P. ^[1] ; de Siervo, Abner ^[2] ; Paixao, Thiago R. L. C. ^[1] ; Munoz, Rodrigo A. A. ^[3] ; Angnes, Lucio ^[1]

Afiliação do(s) autor(es)

^[1] Univ Sao Paulo, Inst Chem, Dept Fundamental Chem, BR-05508000 Sao Paulo, SP - Brazil

^[2] Univ Estadual Campinas, Inst Phys Gleb Wataghin, Dept Appl Phys, BR-13083859 Campinas, SP - Brazil

^[3] Univ Fed Uberlandia, Inst Chem, BR-38400902 Uberlandia, MG - Brazil

• Tipo de documento: Artigo Científico
• Fonte: Microchimica Acta; v. 188, n. 11 NOV 2021.
• Citações Web of Science: 0

Resumo

For the first time the development of an electrochemical method for simultaneous quantification of Zn2+ and uric acid (UA) in sweat is described using an electrochemically treated 3D-printed working electrode. Sweat analysis can provide important information about metabolites that are valuable indicators of biological processes. Improved performance of the 3D-printed electrode was achieved after electrochemical treatment of its surface in an alkaline medium. This treatment promotes the PLA removal (insulating layer) and exposes carbon black (CB) conductive sites. The pH and the square-wave anodic stripping voltammetry technique were carefully adjusted to optimize the method. The peaks for Zn2+ and UA were well-defined at around - 1.1 V and + 0.45 V (vs. CB/PLA pseudo-reference), respectively, using the treated surface under optimized conditions. The calibration curve showed a linear range of 1 to 70 mu g L-1 and 1 to 70 mu mol L-1 for Zn2+ and UA, respectively. Relative standard deviation values were estimated as 4.8% (n = 10, 30 mu g L-1) and 6.1% (n = 10, 30 mu mol L-1) for Zn2+ and UA, respectively. The detection limits for Zn2+ and UA were 0.10 mu g L-1 and 0.28 mu mol L-1, respectively. Both species were determined simultaneously in real sweat samples, and the achieved recovery percentages were between 95 and 106% for Zn2+ and 82 and 108% for UA. (AU)

• Processo FAPESP: 18/14462-0 - Fabricação de dispositivos eletroquímicos em papel visando à aplicação em amostras de interesse clínico e ambiental
• Beneficiário: Vanessa Neiva de Ataide
• Modalidade de apoio: Bolsas no Brasil - Doutorado
• Processo FAPESP: 20/00325-0 - Produção de filamentos condutivos contendo nanomateriais de carbono e nanopartículas metálicas para o desenvolvimento de biossensores eletroquímicos não enzimáticos de baixo custo via manufatura aditiva
• Beneficiário: Diego Pessoa Rocha
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 07/08244-5 - Estudo das propriedades magnéticas de filmes ultrafinos e nanopartículas de Pd e PdAu via XMCD
• Beneficiário: Abner de Siervo
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 07/54829-5 - Estrutura eletrônica e geométrica de nano materiais: um estudo por radiação sincroton
• Beneficiário: Richard Landers
• Modalidade de apoio: Auxílio à Pesquisa - Temático
• Processo FAPESP: 14/50867-3 - INCT 2014: Instituto Nacional de Ciência e Tecnologia de Bioanalítica
• Beneficiário: Marco Aurelio Zezzi Arruda
• Modalidade de apoio: Auxílio à Pesquisa - Temático