The Potentialities of Raman and XPS Techniques to Evaluate the Corrosion Products Formed on the 2198-T851 Aluminium Alloy Exposed to Sodium Chloride Solution

Autor(es)

M. O. A. Ferreira ^[1] ; J. P. L. Nascimento ^[2] ; N. B. Leite ^[3] ; A. de Siervo ^[4] ; G. L. Fernandes ^[5] ; A. R. Vaz ^[6] ; R. V. Gelamo ^[7] ; I. V. Aoki ^[8] ; J. A. Moreto ^[9]

Afiliação do(s) autor(es)

^[1] Universidade Federal do Triângulo Mineiro. Instituto de Ciências Exatas, Naturais e Educação - Brasil

^[2] Universidade Federal do Triângulo Mineiro. Instituto de Ciências Exatas, Naturais e Educação - Brasil

^[3] Universidade Federal do Triângulo Mineiro. Instituto de Ciências Exatas, Naturais e Educação - Brasil

^[4] Universidade Estadual de Campinas. Departamento de Física. Grupo de Ciências de Superfície, Campinas - Brasil

^[5] Universidade Federal de Uberlândia - Brasil

^[6] Universidade Estadual de Campinas. Centro de Componentes Semicondutores e Nanotecnologias - Brasil

^[7] Universidade Federal do Triângulo Mineiro. Instituto de Ciências Tecnológicas e Exatas - Brasil

^[8] Universidade de São Paulo. Escola Politécnica. Departamento de Engenharia Química - Brasil

^[9] Universidade Federal do Triângulo Mineiro. Instituto de Ciências Exatas, Naturais e Educação - Brasil

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 26, 2023-06-30.

Resumo

The aerospace industry is constantly looking for innovative materials that exhibit good mechanical and corrosion properties. The 2198-T851 (Al-Cu-Li) alloy was developed to replace the conventional Al-Cu-Mg in aircraft structures. Despite the usefulness of the 2198-T851 alloy, its performance may be affected when subjected to an aggressive medium containing chloride ions. The deposition of Nb2O5 coatings by using the reactive sputtering technique on the 2198-T851 alloy surface appears as a powerful tool to improve the corrosion resistance of this material. Recently, groundbreaking research findings have demonstrated the positive effect of Nb2O5 coatings on corrosion protection of alloy 2198-T851. However, the corrosion products originated from the 2198-T851 aluminium alloy are poorly understood. The use of Raman spectroscopy and XPS techniques may help to shed some light on the corrosion products of 2198-T851 alloy. Results demonstrated the corrosion products are mainly composed by CuCl2 x H2O, CuCl, Cu2Cl(OH)3, Al(OH)3, and AlO(OH). (AU)