Effect of surface treatments on the localized corrosion resistance of the AA2198-T8 aluminum lithium alloy welded by FSW process

Texto completo
Autor(es):
Machado, Caruline de S. C. ; Klumpp, Rafael E. ; Ayusso, Victor H. ; Donatus, Uyime ; Milagre, Mariana X. ; Araujo, Joao V. de S. ; Machado, Glauson A. F. ; Costa, I.
Número total de Autores: 8
Tipo de documento: Artigo Científico
Fonte: SURFACE AND INTERFACE ANALYSIS; v. 51, n. 12, p. 9-pg., 2019-12-01.
Resumo

In this work, the effect of eight types of surface treatments on the corrosion resistance of friction stir welded samples of an AA2198-T8 Al-Cu-Li alloy were tested and compared in an attempt to find suitable alternatives to toxic and carcinogenic hexavalent chromium treatments. All the samples were anodized and subjected to different post-anodizing treatments. The post-anodizing treatments were (1) hydrothermal treatment in Ce (NO3)(3) 6H(2)O solution; (2) hydrothermal treatment in Ce (NO3)(3) 6H(2)O solution with H2O2; (3) hydrothermal treatment in boiling water; (4) hexavalent chromium conversion coating; and (5) immersion in BTSE (bis-1,2-(triethoxysilyl) ethane. The corrosion resistance of the treated samples was evaluated by immersion tests in sodium chloride solution (0.1 mol L-1 NaCl) and electrochemical impedance spectroscopy (EIS) of the friction stir weldment. The results showed that among the alternative treatments, the Ce-containing solutions presented the best corrosion resistance, especially when used without peroxide. (AU)

Processo FAPESP: 17/03095-3 - Investigação da suscetibilidade à corrosão de ligas Al-Cu-Li com solda por atrito (FSW) utilizando a técnica de varredura do eletrodo vibratório (SVET)
Beneficiário:Uyime Donatus
Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
Processo FAPESP: 13/13235-6 - Estudo da corrosão localizada e caracterização da resistência à corrosão associada à fadiga na região de solda em ligas de alumínio de elevada resistência soldadas por fricção (FSW)
Beneficiário:Isolda Costa
Modalidade de apoio: Auxílio à Pesquisa - Temático