Autor(es)

Vidilli, Andre L. ; Coury, Francisco G. ; Gonzalez, Gonzalo ; Otani, Lucas B. ; Amigo, Vicente ; Bolfarini, Claudemiro

• Tipo de documento: Artigo Científico
• Fonte: METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE; v. 55, n. 1, p. 17-pg., 2023-10-18.

Resumo

In the present study, Ti and B were added to lightweight Fe-Mn-Al-C steels matrix with 0, 0.1, and 0.4 wt pct C in order to evaluate the in-situ formation of reinforcing particles and their influence on the properties. The compositions were tailored by thermodynamic calculations and experimentally validated. Both titanium and boron were introduced in stoichiometry proportions for TiB2 formation. The composites were processed by arc-melting followed by hot rolling and annealing. The experimental results showed that carbon plays a key role in the system since it leads to TiC and (Fe,Mn)(2)B formation and, consequently, reduction of the TiB2 fraction. The composite with the highest Ti, B, and C contents achieved the highest specific modulus value (29.5 GPa cm(3) g(-1)), with a density and modulus of elasticity of 7.09 g cm(-3) and 209.3 GPa, respectively. (AU)

• Processo FAPESP: 16/11309-0 - Estudo, desenvolvimento e aplicação de processo híbrido: Manufatura Aditiva (Ma) + High Speed Machining/Grinding (HSM/G)
• Beneficiário: Reginaldo Teixeira Coelho
• Modalidade de apoio: Auxílio à Pesquisa - Temático
• Processo FAPESP: 20/05049-1 - Design e avaliação das propriedades mecânicas de aços de baixa densidade de alto módulo - com formação de TiB2 in situ - processados por manufatura aditiva e metalurgia do pó
• Beneficiário: André Luiz Vidilli
• Modalidade de apoio: Bolsas no Brasil - Doutorado
• Processo FAPESP: 21/11537-1 - Processamento e caracterização de aços de baixa densidade nanoestruturados reforçados com TiB2 através de manufatura aditiva e metalurgia do pó
• Beneficiário: André Luiz Vidilli
• Modalidade de apoio: Bolsas no Exterior - Estágio de Pesquisa - Doutorado