Effect of Ce³⁺ doping on the structural, optical, and dosimetric properties of magnesium-borate glasses

Autor(es)

Barrera, Gerardo R. ; Almeida, Adriel S. ; Vidigal, Bruno M. ; Silva, Anderson M. B. ; Nunes, Matheus C. S. ; Novais, Andrea L. F. ; Trindade, Neilo M. ; Souza, Divanizia N.

• Tipo de documento: Artigo Científico
• Fonte: Applied Radiation and Isotopes; v. 224, p. 8-pg., 2025-10-01.

Resumo

Ce3+ doped magnesium-borate glasses with compositions 80MgB2O4-20MgB4O7:xCe and 60MgB2O4-40MgB4O7: xCe (where x = 0.10, 0.30, 0.50, 0.70, and 0.90 wt%), were successfully synthesized using the melt quenching method. The physical, structural, and luminescent properties of the glasses were systematically investigated through density measurements, X-ray diffraction (XRD), differential scanning calorimetry (DSC), optical absorption, spectrofluorometry, and optically stimulated luminescence (OSL). XRD patterns confirmed the amorphous nature of the glasses, while DSC provided insights into their thermal stability and phase transition behavior. The thermal stability of the 60 MBO matrix was found to be higher than that of the 80 MBO glass. An increase in glass density with higher Ce3+ concentrations was observed, accompanied by a reduction in molar volume. The indirect and direct optical band gap decreased with increasing Ce3+ content, correlating with the observed decrease in molar volume. Photoluminescence studies revealed emissions associated with Ce3+ ions incorporated into the glass matrix. Additionally, OSL measurements demonstrated the dose-response behavior of the glasses over the range of 0.02-5 Gy. Particularly, the 60MBO glass composition exhibited superior sensitivity to ionizing radiation compared to the 80MBO composition. The OSL signal of the 60MGO glass fades significantly within a few days. Long-term stability of the OSL signal should be a goal for new studies on these glasses. (AU)

• Processo FAPESP: 18/05982-0 - P&D&I em metrologia das radiações na área da saúde
• Beneficiário: Linda Viola Ehlin Caldas
• Modalidade de apoio: Auxílio à Pesquisa - Temático
• Processo FAPESP: 22/14516-8 - Estudo dos mecanismos de luminescência em pastilhas de alexandrita usando luminescência opticamente estimulada
• Beneficiário: Matheus Cavalcanti dos Santos Nunes
• Modalidade de apoio: Bolsas no Exterior - Estágio de Pesquisa - Mestrado
• Processo FAPESP: 24/03006-4 - Luminescência Estimulada de Minerais Simuladores Marcianos e Lunares
• Beneficiário: Neilo Marcos Trindade
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 23/04859-8 - PROPRIEDADES ESTRUTURAIS, ÓPTICAS E DOSIMÉTRICAS DE CRISTAIS DE CaSO4:Mn,Tb: ABORDAGENS COMPUTACIONAIS E EXPERIMENTAIS.
• Beneficiário: Anderson Manoel Bezerra da Silva
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 21/12758-1 - Desenvolvimento e caracterização de um detector de radiação oticamente estimulável baseado na alexandrita natural brasileira
• Beneficiário: Matheus Cavalcanti dos Santos Nunes
• Modalidade de apoio: Bolsas no Brasil - Mestrado
• Processo FAPESP: 19/05915-3 - Caracterização de minerais para dosimetria luminescente das radiações ionizantes
• Beneficiário: Neilo Marcos Trindade
• Modalidade de apoio: Auxílio à Pesquisa - Regular